牌号简介 About |
---|
LNP stat-kon FD000是一种未填充的聚乙烯。这个等级的附加特征是:导电。也称为:lnp*stat-kon*复合F-产品再订购名称:fd000 LNP STAT-KON FD000 is an unfilled Polyethylene. Added feature of this grade is: Electrically Conductive. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ASTM D792 |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
TD:24 hrs TD:24 hrs |
1.0 to 2.0 | % | ASTM D955 |
MD:24 hrs MD:24 hrs |
2.0 to 3.0 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.020 | % | ISO 62 |
24hr,50% RH 24hr,50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture |
MPa | ISO 527-2/5 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture |
% | ISO 527-2/5 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
|||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ 5 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 5 |
|||
23℃ 23℃ 5 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 6 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 6 |
℃ | ISO 75-2/Bf | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-30~30℃ TD:-30~30℃ |
1/℃ | ASTM D696 | |
MD:-30~30℃ MD:-30~30℃ |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2,0 in/min |
3 类型 1, 0,20 in/min |
4 0,051 in/min |
5 80*10*4 |
6 80*10*4 mm |
【新闻资讯】查看全部
欧洲同行:“中国机械制造业”影响力及全球市场份额正在逐步提升
2021-09-12 搜料网资讯: 在《中国制造2025》国家行动纲领和十四五规划(2021-2025)引领下,中国的技术优势和全球市场份额有所提升。 近期发布的《转型中的中国市场》中期报告(以下简称报告 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |