| 牌号简介 About |
|---|
| Lupoy PC 1300-03树脂专为挤出和注塑产品设计。它在耐热性、透明度和冲击强度方面表现出良好的物理性能平衡。 LUPOY PC 1300-03 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. |
产品描述 Product Description
厂家：韩国LG化学 LG Chemical
类别：PC Polycarbonate
用途：包装;复合;电器用具;
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 高粘度; 防火阻燃等级V-2; 耐高温; 透光性好; 冲击性能好; Good Clarity,High impact resistance,High Viscosity,High Heat Resistance,HB,V-2
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.20 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
3.0 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.50 to 0.70 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
0.32 | % | ASTM D570 |
|
23℃，24hr 23℃，24hr |
0.15 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃，3.2mm 23℃，3.2mm 4 |
J/m | ASTM D256 | |
|
23℃ 23℃ |
ASTM D256 | ||
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 5 |
|||
|
23℃，3.20 mm，Total Energy 23℃，3.20 mm，Total Energy 5 |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火，4.0 mm 1.8 MPa, annealed, 4.0 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ASTM D648 | |
|
0.45 MPa，退火，4.0 mm 0.45 MPa, annealed, 4.0 mm |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 6 | |
|
球压温度 Ball pressure temperature |
℃ | IEC 60598-1 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-40~82℃ MD：-40~82℃ |
1/℃ | ASTM D696 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
|||
|
23℃ 23℃ |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
|||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
|||
|
2.00 mm 2.00 mm |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
3.00 mm 3.00 mm |
UL 94 | ||
|
0.50 mm 0.50 mm |
UL 94 | ||
|
1.60 mm 1.60 mm |
UL 94 | ||
|
1.70 mm 1.70 mm |
UL 94 | ||
|
灼热丝起燃温度 Igniting temperature of the hot wire 7 |
|||
|
2 mm 2 mm 7 |
℃ | IEC 60695-2-13 | |
|
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
|
平均燃烧程度 Average combustion degree |
cm | ASTM D635 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
折射率 Refractive index |
ASTM D542 | ||
|
透光率 Transmittance |
% | ASTM D1003 | |
|
雾度 Haze |
% | ASTM D1003 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength 2 |
|||
|
断裂 fracture |
MPa | ASTM D638 | |
|
屈服，23℃ Yield, 23 ℃ 2 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
屈服 yield |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
耐磨耗性 Wear resistance 3 |
|||
|
Change in Haze Change in Haze 3 |
% | ASTM D1004 | |
|
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
|
M 级 M-level |
ASTM D785 | ||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.0 in/min |
| 3 1000g, 500 cycles, CS-10F Wheel |
| 4 9.8 mil 缺口深度 |
| 5 11.1 ft/sec |
| 6 速率 A (50°C/h), 载荷2 (50N) |
| 7 5 sec |
|
【新闻资讯】查看全部 
朗盛展示新型预聚物创新材料
2021-08-22 搜料网资讯： 近日，朗盛聚氨酯系统业务部宣布，在美国犹他州盐湖城举行的聚氨酯制造商协会(PMA)年会上推出Adiprene产品系列中的两种预聚物创新材料研发成果。这两种产品采用低游离 |
|
朗盛展示新型预聚物创新材料 搜料网资讯：近日，朗盛聚氨酯系统业务部宣布，在美国犹他州盐湖城举行的聚氨酯制造商协会(PMA)年会上推出Adiprene产品系列中的两种预聚物创新材料研发成果。这两种产品采用低游离技术制造而成，因此游离二异氰酸酯含量极低。 朗盛聚氨酯系统业务部应用开发经理Ian Laskowitz介绍，聚氨酯浇注系统面临最具挑战性的一个应用是高温应用。多年来，伴随着聚氨酯化学的发展，浇注聚氨酯系统在这一高性能领域中的应用也日益频繁。这种低游离TDI预聚物采用特殊固化剂进行固化。与其他高温应用的预聚物系统相比，这种预聚物更容易加工，加工过程更容易控制，制得的浇注弹性体的性能优异，高温下的撕裂强度几乎不会降低。另外一个优势，即150℃下可以很好地耐受热老化。 朗盛采用己内酰胺(CAP)封端预聚物和二胺固化剂开发了独特的单组分封端预聚物Adiprene K LFM E820，成为PMA年会上高级化学家George Brereton的展示重点。得益于这些采用低游离技术制造的低黏度封端预聚物系统，企业可以利用非传统原料生产出一系列化学品，包括黏度更高的聚碳酸酯多元醇和独特的胺类产品。这些系统对贮存期没有限制，允许加工大型部件，进行复杂的外形设计，并对中空件进行旋转注模。这些系统还能提升热机械性能，降低加工难度，并改进工业卫生。 据了解，封端低游离预聚物的可能应用从仅1~2mm的厚度到重达数吨的大型部件，范围极其广泛。例如，这些系统可用作研磨垫黏合剂或工业滚筒涂料，也可用于工业皮带浸渍。加工人员可以获得的另一项优势是该体系可以单组分加工，无需使用混合和计量系统，由此可以降低部件成本。潜在应用包括用于厚电缆(例如海底电缆)的动态弯曲加强件、工业轧辊、风力涡轮机转子叶片部件或大型复合结构。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
抱歉！该牌号暂无认证数据。
价格走势图
开始时间：
结束时间：
材料厂家：
【牌号齐全，内容全面】
全网共2500+项牌号+上游原料单体+原油价格，最长可追溯近20年价格行情
【精准，及时，权威！】
专业团队挖掘行情信息，第一时间发布行情
抱歉！该牌号暂无认证数据。
免责声明：参考价格是搜料网根据网络大数据拟合分析的结果，仅供参考。实际成交价取决但不限于以下因素：下单时间，付款方式，交货方式，数量，税费，色号，产地，项目信息。
- 后车灯灯壳
- 2019-06-25 0
- Lupoy® 1300-03树脂是注塑成型的聚碳酸酯树脂。它在耐热性、透明度和冲击强度方面表现出良好的物理性能平衡。
- 阅读全文
后车灯灯壳
收起
抱歉！暂无数据。
当前牌号已加入对比
支付宝
微信支付