| 牌号简介 About |
|---|
| Monosol AF L711是一种基于聚乙烯醇的热塑性薄膜，可溶于冷水，使用Monosol AF的专有吹塑薄膜技术制造。Monosol AF L711是一种聚乙烯醇冷水溶性包装膜，设计用于片剂的流动包装和褶皱包装。该薄膜具有良好的硬度，便于在流动包装和褶皱包装设备上加工。可用厚度范围为20微米（0.8密耳）至60微米（2.4密耳）。 Plexiglas® V826 is a thermoplastic acrylic resin formulated for injection molding and extrusion applications. It is characterized by its excellent heat resistance and chemical resistance. Plexiglas® V826 has excellent weatherability and optical properties allowing it to excel in applications requiring outdoor stability, high quality surface appearance and/or precision optics. Plexiglas® V826 is easy to process due to its exceptional thermal stability, extrusion melt strength, and excellent tool surface reproduction and release properties. Supplemental moldflow simulation data is available. It has excellent resistance to many chemicals including solutions of inorganic acids, alkalis and aliphatic hydrocarbons such as VM&P naphtha and heptane. Additionally, it is virtually unaffected by a wide range of commercial products including many beverages, foodstuffs, detergent solutions and cleaners. |
产品描述 Product Description
用途：薄膜;拉伸缠绕;
性能特点： 防火阻燃等级HB; 机械强度好; 水溶性; 生物可降解; 易加工; Good Rigidity,Excellent Processability,Biodegradable,Water soluble,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.18 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，3.80kg 230℃，3.80kg |
1.6 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.20 to 0.60 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
0.30 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
16 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature 2 |
|||
|
1.8 MPa，退火 1.8 MPa, annealed 2 |
℃ | ASTM D648 | |
|
0.45 MPa，退火 0.45 MPa, annealed 2 |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ASTM D1525 3 | |
|
-- -- |
℃ | ASTM D1525 4 | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
折射率 Refractive index 5 |
ASTM D542 | ||
|
透光率 Transmittance |
|||
|
3180 µm 3180 µm |
% | ASTM D1003 | |
|
雾度 Haze |
|||
|
3180 µm 3180 µm |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
ASTM Classification ASTM Classification |
ASTM D788 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
|||
|
屈服 yield |
MPa | ASTM D790 | |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 50%RH |
| 3 Distilled Water (MSTM 205) |
|
【新闻资讯】查看全部 
总投资1000万元！旭氟新材料拟建设聚四氟乙烯塑料制品项目
2020-09-05 搜料网资讯：近日，从扬州市江都区人民政府网站了解到，江苏旭氟新材料有限公司拟建 聚四氟乙烯 塑料制品（塑料薄膜、塑料板材）项目，项目位于扬州市江都区沿江开发区（江苏 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付