PMMA，Plexiglas® V826对比PMMA，Altuglas® V020（已停产）物性表,价格行情_搜料

牌号信息	Plexiglas® V826 物性表 PMMA & 德国罗姆指导价格：暂无塑料库存：缺货	Altuglas® V020（已停产）物性表 PMMA & 美国盛禧奥指导价格：21525.0元/吨塑料库存： 2000kg
牌号简介	Monosol AF L711是一种基于聚乙烯醇的热塑性薄膜，可溶于冷水，使用Monosol AF的专有吹塑薄膜技术制造。Monosol AF L711是一种聚乙烯醇冷水溶性包装膜，设计用于片剂的流动包装和褶皱包装。该薄膜具有良好的硬度，便于在流动包装和褶皱包装设备上加工。可用厚度范围为20微米（0.8密耳）至60微米（2.4密耳）。 Plexiglas® V826 is a thermoplastic acrylic resin formulated for injection molding and extrusion applications. It is characterized by its excellent heat resistance and chemical resistance. Plexiglas® V826 has excellent weatherability and optical properties allowing it to excel in applications requiring outdoor stability, high quality surface appearance and/or precision optics. Plexiglas® V826 is easy to process due to its exceptional thermal stability, extrusion melt strength, and excellent tool surface reproduction and release properties. Supplemental moldflow simulation data is available. It has excellent resistance to many chemicals including solutions of inorganic acids, alkalis and aliphatic hydrocarbons such as VM&P naphtha and heptane. Additionally, it is virtually unaffected by a wide range of commercial products including many beverages, foodstuffs, detergent solutions and cleaners.	Altuglas® V020已停产，是一种聚甲基丙烯酸甲酯-丙烯酸产品,。之前一般原产地为阿科玛韩国工厂。2020年阿科玛关闭韩国工厂，该型号也随之停产。阿科玛目前没有PMMA业务，已将PMMA业务整体出售给盛禧奥。 Altuglas® V020 is a Polymethyl Methacrylate Acrylic product. It is available in Asia Pacific or Europe. Primary characteristic: flame rated.

产品描述
厂家：	德国罗姆 ROHM	美国盛禧奥 Trinseo
类别：	PMMA PMMA	PMMA
填料：
用途：	薄膜,拉伸缠绕
性能特点：	机械强度好,易加工,生物可降解,水溶性,防火阻燃等级HB Good Rigidity,Excellent Processability,Biodegradable,Water soluble,HB
加工条件：

技术参数

物理性能
PHYSICAL Plexiglas® V826 Altuglas® V020（已停产）单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D955

熔体质量流动速率(230℃，3.80kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT Plexiglas® V826 Altuglas® V020（已停产）单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁无缺口冲击强度
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁缺口冲击强度
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL Plexiglas® V826 Altuglas® V020（已停产）单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(0.45 MPa，退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 3

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 4

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 3

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 4

阻燃性能
FLAMMABILITY Plexiglas® V826 Altuglas® V020（已停产）单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

光学性能
OPTICAL Plexiglas® V826 Altuglas® V020（已停产）单位
UNIT 测试方法
TEST METHOD

折射率
Refractive index ASTM D542

透光率
Transmittance % ASTM D1003

透光率(3180 µm)
Transmittance % ASTM D1003

雾度
Haze % ASTM D1003

雾度(3180 µm)
Haze % ASTM D1003

补充信息
Plexiglas® V826 Altuglas® V020（已停产）单位
UNIT 测试方法
TEST METHOD

ASTM Classification
ASTM Classification ASTM D788

机械性能
MECHANICAL Plexiglas® V826 Altuglas® V020（已停产）单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度(屈服)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

洛氏硬度(M 级)
Rockwell hardness ASTM D785

加工方式

注射 Plexiglas® V826 Altuglas® V020（已停产）单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议注射量 %

建议的最大回制料比例 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

背压 MPa

螺杆压缩比

螺杆转速 rpm

螺杆长径比

加工温度 Plexiglas® V826 Altuglas® V020（已停产）单位测试方法

中筒温度 ℃

前筒温度 ℃

后筒温度 ℃

喷嘴温度 ℃

模具温度 ℃

预热时间 hr

预热温度 ℃

备注

1 一般属性：这些不能被视为规格。

2 50%RH

3 Distilled Water (MSTM 205)

3、速率 A (50°C/h), 压力1 (10N)

4、速率 A (50°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
阻燃性能
光学性能
补充信息
机械性能
加工方式
注射
加工温度
备注
返回顶部

PMMA，Plexiglas® V826对比PMMA，Altuglas® V020（已停产）对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别