牌号简介 About |
---|
PRIMACOR™ 1430是一种乙烯-丙烯酸共聚物,具有良好的密封性、热粘性和极性(箔、尼龙等)材料的良好粘附性。它还提供出色的韧性,清晰度和抗撕裂性。用于吹塑或铸膜挤出的软包装结构中密封剂层的粘合层,在需要与尼龙或箔粘合的情况下使用,符合:美国FDA 21 CFR 177.1310(a)(1)欧盟,第10/2011号。有关完整细节,请参考法规。 PRIMACOR™ 1430 is an ethylene acrylic acid copolymer that provides good sealability, hot tack and excellent adhesion to polar (foil, nylon, etc.) materials. It also provides excellent toughness, clarity and tear resistance. Adhesive layer of sealant layer in flexible packaging structures For blown or cast film extrusion Used where adhesion to nylon or foil is desired Complies with: U.S. FDA 21 CFR 177.1310(a)(1) EU, No 10/2011 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.930 | g/cm³ | ASTM D792 , ISO 1183 |
熔体质量流动速率 Melt Flow Rate 2 |
|||
190℃,2.16kg 190℃,2.16kg 2 |
5.0 | g/10min | ASTM D1238,ISO 1133 |
共聚单体含量 Co monomer content 3 |
9.7 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding 4 |
7.67 | MPa | ASTM D638 |
屈服,模压成型 Yield, molding |
7.67 | MPa | ISO 527-2/508 |
断裂,模压成型 Fracture, molded 4 |
MPa | ASTM D638 | |
断裂,模压成型 Fracture, molded |
MPa | ISO 527-2/508 | |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded 4 |
% | ASTM D638 | |
断裂,模压成型 Fracture, molded |
% | ISO 527-2/508 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ISO 527-3 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ISO 527-3 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 , ISO 527-3 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 , ISO 527-3 | |
拉伸应变 Tensile strain |
ASTM D882 , ISO 527-3 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 , ISO 527-3 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 , ISO 527-3 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 5 |
|||
MD:51 µm MD:51 µm |
g | ASTM D1922 | |
TD:51 µm TD:51 µm |
g | ASTM D1922 | |
MD:51 µm MD:51 µm |
N | ISO 6383-2 | |
TD:51 µm TD:51 µm |
N | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 , ISO 306 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.8 µm 45°,50.8 µm |
ASTM D2457 | ||
雾度 Haze |
|||
50.8 µm 50.8 µm |
% | ASTM D1003 | |
50.8 µm 50.8 µm |
% | ISO 14782 |
备注 |
---|
2 如同在生产时测量的一样。 |
3 通过 Dow 属性方法测量的共聚单体含量,和 ASTM D 4094 相比具有相同的精确性。 |
4 510 mm/min |
5 通过 DOW 属性方法测量的共聚单体含量,和 ASTM D 4094 相比具有相同的精确性。 |
【新闻资讯】查看全部
请留意,你的电子外壳有螺丝孔开裂隐患!
2019-12-03 上篇说到, 3C电子外壳材料因为需要阻燃性、强韧平衡、能薄壁成型以及尺寸稳定性,所以无卤阻燃PC/ABS是最优的选择 。 然而,无卤阻燃PC/ABS也不是万能的,用它做3C电子外壳产品,一 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |