EMERGE™ PC 8330-22高级树脂是一种透明的阻燃PC树脂,不含氯化、溴化或磷基添加剂。树脂设计符合德国标准DIN VDE-0472/第815部分关于卤素的要求。该树脂具有良好的机械性能和高热性能,保持良好的加工性能,含有脱模剂,并具有紫外线稳定性。Emerge PC 8330-22的UL 94 V-0额定值为2.5 mm。应用:电气外壳显示照明 EMERGE™ PC 8330-22 advanced resin is a transparent, ignition resistant PC resin that contains no chlorinated or brominated or phosphorous based additives. The resin is designed to meet the German norm DIN VDE-0472/Part 815 on halogens. This resin combines good mechanical and high heat properties and maintains excellent processability, contains mould release agent and is UV stabilized. EMERGE ™ PC 8330-22 has a UL 94 V-0 rating at 2.5 mm. Applications: Electrical Enclosures Display Lighting |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183/B |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
22 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.50 to 0.70 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2400 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
断裂 fracture |
70.0 | MPa | ISO 527-2 |
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压温度 Ball pressure temperature |
℃ | IEC 60335-1 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
IEC 60250 | ||
1 Hz 1 Hz |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
1 Hz 1 Hz |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 2 |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
2.50 mm 2.50 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index 2 |
IEC 60695-2-12 | ||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire 2 |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
氧指数 Oxygen index 2 |
% | ISO 4589-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance 3 |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
3 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
4 standard tints |
【新闻资讯】查看全部
日本帝人研发出碳纤维全新模压成型工艺
2020-12-25 化学品和食品原料制造商Adeka和帝人集团复合材料结构设计、开发和评价业务子公司GH Craft宣布,共同研发出了全新的Fiber-to-Composite(FtoC)模压成型工艺,能够在开放模具中制备纤维增强复合材料 |
日本帝人研发出碳纤维全新模压成型工艺 化工品和食品生产商Adeka和帝人集团公司复合材料总体设计、开发设计和点评业务流程分公司GH Craft公布,相互产品研发出了全新升级的Fiber-to-Composite(FtoC)模压成型工艺,可以在对外开放磨具中制取纤维提高复合材料(FRP)聚酰亚胺薄膜。
FtoC模压工艺可以全自动开展树脂预浸、干固和压层工艺流程,另外得到 高取向度的纤维排序方法。Adeka所开发设计的一种独特的迅速干固环氧树脂树脂可以在GH Craft开发设计的红外辐射成形工艺标准下经几十秒迅速干固。工艺全过程不用固化炉、工作压力磨具等大中型机器设备,只需在对外开放磨具中压层进行。 与传统式复合材料生产制造工艺对比,因为FtoC模压工艺根据立即将纤维模压到复合材料上省去了正中间全过程,因而大幅度降低了纤维废弃物。此外,根据纤维的延伸和趋向化,该工艺可以明显提升玻璃纤维复合材料(GFRP)的特性,与传统式树脂传送橡塑制品成形工艺(RTM)制取的GFRP对比,弯曲强度提升100%,抗拉强度提升40%,固层剪切强度提升75%。 将来,Adeka将为FtoC模压工艺开发设计系列产品专用型树脂,GH Craft也将开发设计该工艺的具体运用。彼此将根据具体商品的生产制造来认证FtoC模压工艺的实际效果。此外,彼此的相互总体目标是根据将FtoC模压工艺开设为复合材料生产制造的具体规范,而造就出一个新的复合材料销售市场行业。 FRP由具备一定取向度的单边纤维预浸常规树脂后经加温模压成型。热压罐、RTM等传统式热固性塑料树脂成形工艺具备生产制造时间长、产品成本高的特性,必须固化炉、工作压力磨具等机器设备才可以生产制造大中型构件,另外因为存有正中间裁剪流程而导致很多的纤维消耗。此外,传统式的热固性塑料树脂成形工艺会使纤维在常规树脂中产生歪曲而丧失高趋向性,进而难以得到 高强度FRP。
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |