牌号简介 About |
---|
可用于连接器的通用PBT材料 Infino GP-5000 is a Polybutylene Terephthalate (PBT) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Electrical/Electronic Applications. Primary characteristic: flame rated. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
- - |
1.30 | g/cm³ | ISO 1183 |
|
1.31 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,2.16kg 250℃,2.16kg |
74 | g/10min | ASTM D1238 |
250℃,2.16kg 250℃,2.16kg |
71 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
1.2 to 2.1 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 6 |
|||
23℃ 23℃ 6 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃ 23℃ 6 |
kJ/m² | ISO 180-1A | |
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ISO 75-2/A | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,4.0 mm 0.45 MPa, unannealed, 4.0 mm |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
IEC 60250 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
IEC 60250 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance 7 |
sec | ASTM D495 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.70 mm 0.70 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 2 |
MPa | ASTM D638 | |
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain 4 |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 4 |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 |
MPa | ISO 178 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
R 级 R-level |
ISO 2039-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.20 in/min |
4 0.11 in/min |
5 0.079 in/min |
6 Thickness: 4mm |
7 Tungsten |
【新闻资讯】查看全部
索尼拟加工工厂自动化 利用机器人大幅削减成本
2021-07-12 搜料网资讯: 索尼公司预计,随着公司将业务中心转移到服务领域,机器人将接管电视、智能手机和相机的生产。 该公司电子业务主管Kimio Mak表示,到2023财年,索尼在马来西亚的主要 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |