| 牌号简介 About |
|---|
| Polifil C系列化合物是用细颗粒碳酸钙增强的均聚聚丙烯树脂。它们结合了高冲击和刚度，热老化，良好的着色性，耐环境应力开裂，良好的表面和低的模具收缩。这些化合物用于电器、电器元件、家庭用品、玩具、汽车和公用事业产品。适用标准加工技术。使用此信息作为指南，帮助您选择适合您应用的树脂。TPG将为您的应用定制化合物并微调我们的配方。 Polifil ® C series compounds are homopolymer polypropylene resins reinforced with fine particle size calcium carbonate. They combine high impact with stiffness, good colorability, resistance to environmental stress-cracking, good surface, and low mold shrinkage. Polifil ® C products in the 20 to 40% range are UL94 HB rated. These compounds are used in appliances, electrical components, housewares, toys, automotive, and utility products. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application. |
产品描述 Product Description
用途：电气元件;汽车领域的应用;家用货品;玩具;电器用具;
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 着色性好; 均聚物; 收缩性低; 抗应力开裂; 表面光泽度好; 耐老化; Good Rigidity,Good heat aging resistance,Good surface appearance,Low contractility,High ESCR,Homopolymer,Good coloring
填料：碳酸钙
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.978 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
8.0 到 12 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
1.5 | % | ASTM D955 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
37 | J/m | ASTM D256 |
|
落锤冲击 Drop hammer impact |
|||
|
23℃，12.7 mm 23℃，12.7 mm |
2.71 | J | ASTM D3029 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ASTM D1415 | ||
|
拉伸模量 Tensile modulus |
|||
|
23℃ 23℃ |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
|||
|
23℃ 23℃ |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
ASTM D638 | ||
|
屈服，23℃ Yield, 23 ℃ |
% | ASTM D638 | |
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
正切，23℃ Tangent, 23 ℃ |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
2020年我国钛白粉总产量达到351万吨
2021-01-21 搜料网资讯： 1月20日，记者从化工生产力促进中心钛白分中心和钛白粉产业技术创新战略联盟秘书处获悉，据钛白分中心和钛白粉联盟秘书处最新统计，2020年全国所有42家全流程型钛白 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付