牌号简介 About |
---|
MALECCA是一种基于苯乙烯-N-苯基马来酰亚胺共聚物的高耐热ABS树脂。马六甲是由丹卡公司利用其先进的聚合技术开发的。与传统的α-甲基苯乙烯树脂相比,这种高热ABS在热稳定性、加工特性和冲击强度方面得到了更大的改善,并且非常容易使用。 MALECCA is a high heat resistant ABS resin which is based on styrene-N-phenylmaleimide copolymer. MALECCA was developed by Denka using their advanced polymerization technologies. This high heat ABS is much more highly improved in the areas of heat stability, processing characteristics and impact strength over traditional alpha-methylstyrene-based resins and is very easy to use. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate Melt Flow Rate |
|||
220℃,98N 220℃,98N |
2 | g/10min | ISO 1133 |
265℃,98N 265℃,98N |
22 | g/10min | ISO 1133 |
密度 Density Density |
|||
|
1080 | kg/m³ | ISO 1183 |
|
1.08 | g/cm³ | ASTM D792 |
成型收缩率 Molding Shrinkage Molding shrinkage |
0.5-0.8 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
1 mm/min 1 mm/min |
MPa | ISO 527 | |
5 mm/min 5 mm/min |
MPa | ASTM D638 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
屈服 yld,50 mm/min Yield yld, 50 mm/min |
MPa | ISO 527-2 | |
断裂 brk,50 mm/min Broken BRK, 50 mm/min |
MPa | ISO 527-2 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
2 mm/min 2 mm/min |
MPa | ISO 178 | |
15 mm/min 15 mm/min |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
2 mm/min 2 mm/min |
MPa | ISO 178 | |
15 mm/min 15 mm/min |
MPa | ASTM D790 | |
洛氏硬度 Rockwell Hardness Rockwell hardness |
|||
|
R Scale | ISO 2039-2 | |
|
R Scale | ASTM D-785 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa 1.8 MPa |
℃ | ISO 75-1/-2 | |
1.82 MPa 1.82 MPa |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
|||
|
℃ | ISO 306/B | |
|
℃ | ASTM D1525 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 0.59 in/min |
4 0.079 in/min |
5 Edgewise |
6 载荷2 (50N) |
【新闻资讯】查看全部
中国第一套离子液体催化乙烯甲基丙烯酸甲酯新技术投产
2022-07-04 30万吨甲基丙烯酸甲酯一期工程开工 7月1日,河南中科普原料新材料有限公司30万吨甲基丙烯酸甲酯(以下简称MMA)一期工程开工仪式在濮阳经济技术开发区举行,标志着中国科学院和中 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |