ABS，MALECCA K-400对比ABS，Toyolac® 470Y-X68物性表,价格行情_搜料

牌号信息	MALECCA K-400 物性表 ABS & 日本电化指导价格：暂无塑料库存：缺货	Toyolac® 470Y-X68 物性表 ABS & 日本东丽指导价格：暂无塑料库存：缺货
牌号简介	MALECCA是一种基于苯乙烯-N-苯基马来酰亚胺共聚物的高耐热ABS树脂。马六甲是由丹卡公司利用其先进的聚合技术开发的。与传统的α-甲基苯乙烯树脂相比，这种高热ABS在热稳定性、加工特性和冲击强度方面得到了更大的改善，并且非常容易使用。 MALECCA is a high heat resistant ABS resin which is based on styrene-N-phenylmaleimide copolymer. MALECCA was developed by Denka using their advanced polymerization technologies. This high heat ABS is much more highly improved in the areas of heat stability, processing characteristics and impact strength over traditional alpha-methylstyrene-based resins and is very easy to use.	Toyolac® 470Y-X68是一种丙烯腈丁二烯苯乙烯(ABS)产品,。它,在北美洲、欧洲或亚太地区有供货。特性包括: 阻燃/额定火焰耐磨耐热 Toyolac® 470Y-X68 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Asia Pacific, Europe, or North America. Applications of Toyolac® 470Y-X68 include appliances and electrical/electronic applications. Characteristics include: Flame Rated Heat Resistant Wear Resistant

产品描述
厂家：	日本电化 Denka	日本东丽 Toray
类别：	ABS	ABS ABS
填料：
用途：
性能特点：	防火阻燃等级HB HB	耐高温,耐磨,防火阻燃等级HB High Heat Resistance,Good wear resistance,HB
加工条件：	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL MALECCA K-400 Toyolac® 470Y-X68 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

密度 Density()
Density g/cm³ ASTM D792

密度 Density()
Density g/cm³ ISO 1183

成型收缩率 Molding Shrinkage
Molding shrinkage % 内部方法

收缩率
Shrinkage rate % 内部方法

熔体质量流动速率 Melt Flow Rate(220℃，98N)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率 Melt Flow Rate(265℃，98N)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL MALECCA K-400 Toyolac® 470Y-X68 单位
UNIT 测试方法
TEST METHOD

弯曲强度 Flexural Strength(15 mm/min)
Flexural Strength MPa ASTM D790

弯曲强度 Flexural Strength(2 mm/min)
Flexural Strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量 Flexural Modulus(15 mm/min)
Flexural Modulus MPa ASTM D790

弯曲模量 Flexural Modulus(2 mm/min)
Flexural Modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度 Tensile Strength(屈服 yld，50 mm/min)
Tensile Strength MPa ISO 527-2

拉伸强度 Tensile Strength(断裂 brk，50 mm/min)
Tensile Strength MPa ISO 527-2

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2

拉伸模量 Tensile Modulus(1 mm/min)
Tensile Modulus MPa ISO 527

拉伸模量 Tensile Modulus(5 mm/min)
Tensile Modulus MPa ASTM D638

洛氏硬度 Rockwell Hardness()
Rockwell hardness R Scale ASTM D-785

洛氏硬度 Rockwell Hardness()
Rockwell hardness R Scale ISO 2039-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

冲击性能
IMPACT MALECCA K-400 Toyolac® 470Y-X68 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度 Izod Notched Impact strength
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃，12.7mm)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁缺口冲击强度 Charpy notched Impact strength
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL MALECCA K-400 Toyolac® 470Y-X68 单位
UNIT 测试方法
TEST METHOD

热变形温度 HDT(1.8 MPa)
Hot deformation temperature HDT ℃ ISO 75-1/-2

热变形温度 HDT(1.82 MPa)
Hot deformation temperature HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

维卡软化温度
Vicat Softening Temp ℃

维卡软化温度 Vicat Softening Temperature()
Vicat Softening Temperature ℃ ASTM D1525

维卡软化温度 Vicat Softening Temperature()
Vicat Softening Temperature ℃ ISO 306/B

阻燃性能
FLAMMABILITY MALECCA K-400 Toyolac® 470Y-X68 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

阻燃等级 Flame Class Rating
Flame Class Rating UL 94

加工方式

注塑成型 Injection Molding MALECCA K-400 Toyolac® 470Y-X68 单位测试方法

中段温度 Middle Temperature -Zone 2 °C

前段温度 Front Temperature -Zone 3 °C

后段温度 Rear Temperature -Zone 1 °C

喷嘴温度 Nozzle Temperature °C

干燥时间 Drying Time hr

干燥温度 Drying Temperature °C

模具温度 Mold Temperature °C

背压 Back Pressure [kg/cm²・G

螺杆转速 Screw Speed rpm

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 0.59 in/min

4 0.079 in/min

5 Edgewise

6 载荷2 (50N)

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注塑成型 Injection Molding
备注