牌号简介 About |
---|
Lofex A311A是一种光学透明的聚酯薄膜,其内电晕/外压克力通过增强对油墨和涂层的粘附力进行处理。因此,它可以被窗口胶卷、标签和印刷胶卷所使用。同时,通过拉伸强度、适当的延伸率和热收缩率使其具有优异的性能。 LOFEX ® A311A is Polyester film is optically clear and inside corona / outside acryl treated with enhanced adhesion to inks and coatings. So, it can use by window film, label and print film. Also, it has excellent properties by tensile strength, proper elongation and the thermal contraction rate. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态 With oneself - dynamic |
0.30 | ASTM D1894 | |
与自身 - 静态 With oneself - static |
0.35 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,50 µm MD, yield, 50 µ m |
196 | MPa | ASTM D882 |
MD,屈服,100 µm MD, yield, 100 µ m |
196 | MPa | ASTM D882 |
TD,屈服,50 µm TD, yield, 50 µ m |
235 | MPa | ASTM D882 |
TD,屈服,100 µm TD, yield, 100 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,50 µm MD, fracture, 50 µ m |
% | ASTM D882 | |
MD,断裂,100 µm MD, fracture, 100 µ m |
% | ASTM D882 | |
TD,断裂,50 µm TD, fracture, 50 µ m |
% | ASTM D882 | |
TD,断裂,100 µm TD, fracture, 100 µ m |
% | ASTM D882 | |
F5 F5 |
ASTM D882 | ||
MD:50.0 µm MD:50.0 µm |
MPa | ASTM D882 | |
MD:100.0 µm MD:100.0 µm |
MPa | ASTM D882 | |
TD:50.0 µm TD:50.0 µm |
MPa | ASTM D882 | |
TD:100.0 µm TD:100.0 µm |
MPa | ASTM D882 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D523 | ||
60°,50.0 µm 60°,50.0 µm |
ASTM D523 | ||
60°,100 µm 60°,100 µm |
ASTM D523 | ||
透光率 Transmittance |
ASTM D1003 | ||
50.0 µm 50.0 µm |
% | ASTM D1003 | |
100 µm 100 µm |
% | ASTM D1003 | |
雾度 Haze |
ASTM D1003 | ||
50 µm 50 µm |
% | ASTM D1003 | |
100 µm 100 µm |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热收缩 Thermal shrinkage |
内部方法 | ||
MD,30 min:150℃,50.0 µm MD,30 min:150℃,50.0 µm |
% | 内部方法 | |
MD,30 min:150℃,100.0 µm MD,30 min:150℃,100.0 µm |
% | 内部方法 | |
TD,30 min:150℃,50.0 µm TD,30 min:150℃,50.0 µm |
% | 内部方法 | |
TD,30 min:150℃,100.0 µm TD,30 min:150℃,100.0 µm |
% | 内部方法 | |
Surface Treatment Surface Treatment |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
湖北乙烯塑料产业链对接会在汉成功召开
2016-06-13 为贯彻全省一季度工业经济形势分析会精神,推动乙烯产业上下游联动发展,做长做深我省乙烯产业链条,填补我省有机化工发展短板,5月27日,省经信委在汉召开全省乙烯塑料产业链对接会,吸引了来自省内外82家乙烯、塑料企业共商合作、深度对接。省政府副秘书长贺盛有出席会议并讲话,吴方军副主任通报活动筹备情况及产业对接具体要求,武汉化工园交流了乙烯产业发展及规划情况,中韩石化、中石化华中销售公司、宜化集团、凯乐集团、顾地科技、宜然塑胶等企业交流发言,中石化华中销售公司分别与顾地科技、武汉金发科技签订合作协 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |