PET，LOFEX® A311A对比PET，LOFEX® A31AA物性表,价格行情_搜料

牌号信息	LOFEX® A311A 物性表 PET & 韩国乐天指导价格：暂无塑料库存：缺货	LOFEX® A31AA 物性表 PET & 韩国乐天指导价格：暂无塑料库存：缺货
牌号简介	Lofex A311A是一种光学透明的聚酯薄膜，其内电晕/外压克力通过增强对油墨和涂层的粘附力进行处理。因此，它可以被窗口胶卷、标签和印刷胶卷所使用。同时，通过拉伸强度、适当的延伸率和热收缩率使其具有优异的性能。 LOFEX ® A311A is Polyester film is optically clear and inside corona / outside acryl treated with enhanced adhesion to inks and coatings. So, it can use by window film, label and print film. Also, it has excellent properties by tensile strength, proper elongation and the thermal contraction rate.	Lofex A31aa是一种光学透明的聚酯薄膜，两面均经过压克力处理，增强了对油墨和涂层的粘附力。所以，它可以用图形、薄膜开关、标签、电路板。通过拉伸强度、适当的延伸率和热收缩率，该材料具有优良的性能。另外，它是一种可以根据客户需求进行厚度控制的产品。 LOFEX ® A31AA is Polyester film is optically clear and both sides acryl treated with enhanced adhesion to inks and coatings. So, it can use by graphic, membrane switch, label, circuit board. It has excellent properties by tensile strength, proper elongation and the thermal contraction rate. Also, it is a product that thickness control is possible according to customer needs.

产品描述
厂家：	韩国乐天 LOTTE	韩国乐天 LOTTE
类别：	PET PET	PET PET
填料：
用途：	薄膜,工业应用,标签	薄膜按键开关,印刷电路板,工业应用
性能特点：	机械强度好,透光性好 Good Rigidity,Good Clarity	机械强度好,透光性好 Good Rigidity,Good Clarity
加工条件：

技术参数

机械性能
MECHANICAL LOFEX® A311A LOFEX® A31AA 单位
UNIT 测试方法
TEST METHOD

摩擦系数(与自身 - 动态)
friction coefficient ASTM D1894

摩擦系数(与自身 - 静态)
friction coefficient ASTM D1894

薄膜
LOFEX® A311A LOFEX® A31AA 单位
UNIT 测试方法
TEST METHOD

F5(MD：100.0 µm)
F5 MPa ASTM D882

F5(MD：125.0 µm)
F5 MPa ASTM D882

F5(MD：188.0 µm)
F5 MPa ASTM D882

F5(MD：50.0 µm)
F5 MPa ASTM D882

F5(TD：100.0 µm)
F5 MPa ASTM D882

F5(TD：125.0 µm)
F5 MPa ASTM D882

F5(TD：188.0 µm)
F5 MPa ASTM D882

F5(TD：50.0 µm)
F5 MPa ASTM D882

拉伸应变(MD，断裂，100 µm)
Tensile strain % ASTM D882

拉伸应变(MD，断裂，130 µm)
Tensile strain % ASTM D882

拉伸应变(MD，断裂，190 µm)
Tensile strain % ASTM D882

拉伸应变(MD，断裂，50 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，100 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，130 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，190 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，50 µm)
Tensile strain % ASTM D882

拉伸强度(MD，屈服，100 µm)
tensile strength MPa ASTM D882

拉伸强度(MD，屈服，130 µm)
tensile strength MPa ASTM D882

拉伸强度(MD，屈服，190 µm)
tensile strength MPa ASTM D882

拉伸强度(MD，屈服，50 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，100 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，130 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，190 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，50 µm)
tensile strength MPa ASTM D882

光学性能
OPTICAL LOFEX® A311A LOFEX® A31AA 单位
UNIT 测试方法
TEST METHOD

光泽度(60°，100 µm)
gloss ASTM D523

光泽度(60°，125 µm)
gloss ASTM D523

光泽度(60°，188 µm)
gloss ASTM D523

光泽度(60°，50.0 µm)
gloss ASTM D523

透光率(100 µm)
Transmittance % ASTM D1003

透光率(125 µm)
Transmittance % ASTM D1003

透光率(188 µm)
Transmittance % ASTM D1003

透光率(50.0 µm)
Transmittance % ASTM D1003

雾度(100 µm)
Haze % ASTM D1003

雾度(125 µm)
Haze % ASTM D1003

雾度(188 µm)
Haze % ASTM D1003

雾度(50 µm)
Haze % ASTM D1003

补充信息
LOFEX® A311A LOFEX® A31AA 单位
UNIT 测试方法
TEST METHOD

Surface Treatment
Surface Treatment

热收缩(MD，30 min：150℃，100.0 µm)
Thermal shrinkage % 内部方法

热收缩(MD，30 min：150℃，125.0 µm)
Thermal shrinkage % 内部方法

热收缩(MD，30 min：150℃，188.0 µm)
Thermal shrinkage % 内部方法

热收缩(MD，30 min：150℃，50.0 µm)
Thermal shrinkage % 内部方法

热收缩(TD，30 min：150℃，100.0 µm)
Thermal shrinkage % 内部方法

热收缩(TD，30 min：150℃，125.0 µm)
Thermal shrinkage % 内部方法

热收缩(TD，30 min：150℃，188.0 µm)
Thermal shrinkage % 内部方法

热收缩(TD，30 min：150℃，50.0 µm)
Thermal shrinkage % 内部方法

备注

1 一般属性：这些不能被视为规格。