牌号简介 About |
---|
Borcoat™ EB133E-1199-LT是一种基于聚丙烯共聚物的弹性体改性化合物。具有优异的耐低温冲击性能。产品为白色。该产品具有热稳定性和紫外线稳定性。产品以颗粒形式提供。 Borcoat EB133E-1199-LT is an elastomer modified compound, based on polypropylene copolymer. It has excellent low temperature impact resistance. The product is coloured white. It includes a combination of stabilisers to ensure long-term thermal stability. The product is supplied in pellet form Applications Borcoat EB133E-1199-LT is recommended as a top coat for multilayer PP systems and thermal insulation used in: Steel Pipe Coating Specifications Borcoat EB133E-1199-LT is intended to fulfil following National and International standards, when appropriate industrial manufacturing standard procedures are applied and a continuous quality system is implemented and when used in combination with Borcoat™ BB122E-LT and a compatible powder epoxy. ISO 21809-1 DIN 30678 NF A49-711 Gazprom 2-2.2-178-2007 Due to the nature of the modified PP material, indentation resistance of the applied coating could be borderline versus some requirements of common standards and due to known variations in testing, those specified values should be separately agreed upon between the applicator and the client (end user/purchaser). Special Features Borcoat EB133E-1199-LT is intended for design temperatures between -20°C and +110°C and tailored for low temperature handling, transportation and installation. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 3 |
0.915 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
1.0 | g/10min | ISO 1133 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
10%非离子洗涤剂,F50 10% non-ionic detergent, F50 |
> 3000 | hr | ASTM D1693A |
Moisture Moisture |
< 0.050 | % | Karl Fisher |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,3 秒 Shore D, 3 seconds |
60 | ISO 868 | |
拉伸模量 Tensile modulus |
|||
1 mm 1 mm |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield |
% | ISO 527-2/50 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
-20℃ -20℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
氧化诱导时间 Oxidation induction time |
|||
220℃ 220℃ |
min | ISO 11357 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Compound |
【新闻资讯】查看全部
西门子在华启动“零碳先锋计划”
2021-09-25 搜料网资讯: 图为启动仪式现场。 近日,西门子中国正式启动零碳先锋计划。西门子提出,将以数字化创新和跨领域知识与经验,在中国携手各方伙伴共创绿色生态,赋能打造端到端的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |