PP共聚，Borcoat™ EB133E-1199-LT对比PP共聚，ExxonMobil™ PP7011L1物性表,价格行情_搜料

牌号信息	Borcoat™ EB133E-1199-LT 物性表 PP共聚 & 奥地利北欧化工指导价格：暂无塑料库存：缺货	ExxonMobil™ PP7011L1 物性表 PP共聚 & 美国埃克森美孚指导价格：暂无塑料库存：缺货
牌号简介	Borcoat™ EB133E-1199-LT是一种基于聚丙烯共聚物的弹性体改性化合物。具有优异的耐低温冲击性能。产品为白色。该产品具有热稳定性和紫外线稳定性。产品以颗粒形式提供。 Borcoat EB133E-1199-LT is an elastomer modified compound, based on polypropylene copolymer. It has excellent low temperature impact resistance. The product is coloured white. It includes a combination of stabilisers to ensure long-term thermal stability. The product is supplied in pellet form Applications Borcoat EB133E-1199-LT is recommended as a top coat for multilayer PP systems and thermal insulation used in: Steel Pipe Coating Specifications Borcoat EB133E-1199-LT is intended to fulfil following National and International standards, when appropriate industrial manufacturing standard procedures are applied and a continuous quality system is implemented and when used in combination with Borcoat™ BB122E-LT and a compatible powder epoxy. ISO 21809-1 DIN 30678 NF A49-711 Gazprom 2-2.2-178-2007 Due to the nature of the modified PP material, indentation resistance of the applied coating could be borderline versus some requirements of common standards and due to known variations in testing, those specified values should be separately agreed upon between the applicator and the client (end user/purchaser). Special Features Borcoat EB133E-1199-LT is intended for design temperatures between -20°C and +110°C and tailored for low temperature handling, transportation and installation.	一种适用于挤出场合的抗冲击共聚物树脂，它具有高熔融粘度和优异的低温抗冲击强度。它适用于电缆、管道、型材、片材和热成型。一种适用于挤出场合的抗冲击共聚物树脂，它具有高熔融粘度和优异的低温抗冲击强度。它适用于电缆、管道、型材、片材和热成型。

产品描述
厂家：	奥地利北欧化工 Borealis AG	美国埃克森美孚 ExxonMobil
类别：	PP共聚 PP copolymer	PP共聚 PP copolymer
填料：
用途：	管线涂料	工业应用,电气/电子应用领域,复合,波纹管
性能特点：	可回收,耐低温冲击,热稳定性好 Renewable resources,low-temperature impact resistance,Heat Stabilized	流动性低,冲击性能好 Low liquidity,High impact resistance
加工条件：	挤出 Extrusion	挤出 Extrusion

技术参数

物理性能
PHYSICAL Borcoat™ EB133E-1199-LT ExxonMobil™ PP7011L1 单位
UNIT 测试方法
TEST METHOD

Moisture
Moisture % Karl Fisher

密度
Density g/cm³ ISO 1183

抗环境应力开裂(10%非离子洗涤剂，F50)
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693A

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(230℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL Borcoat™ EB133E-1199-LT ExxonMobil™ PP7011L1 单位
UNIT 测试方法
TEST METHOD

弯曲模量(正割)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(1 mm)
Tensile modulus MPa ISO 527-2

拉伸模量(正割)
Tensile modulus MPa ISO 527-1-2

邵氏硬度(邵氏 D)
Shore hardness ISO 868

邵氏硬度(邵氏 D，3 秒)
Shore hardness ISO 868

冲击性能
IMPACT Borcoat™ EB133E-1199-LT ExxonMobil™ PP7011L1 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃，局部断裂)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(-20℃，完全断裂)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(0℃，完全断裂)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃，局部断裂)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL Borcoat™ EB133E-1199-LT ExxonMobil™ PP7011L1 单位
UNIT 测试方法
TEST METHOD

氧化诱导时间(220℃)
Oxidation induction time min ISO 11357

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

加工方式

挤出 Borcoat™ EB133E-1199-LT ExxonMobil™ PP7011L1 单位测试方法

口模温度 °C

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

料筒5区温度 °C

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 Compound

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
挤出
备注