| 牌号简介 About |
|---|
| CELCON缩醛共聚物M140级是中等高流动性通用注射成型级。它设计用于需要在标准Celcon M90材料上增强流动特性的应用中。符合ISO 1043-1的化学缩写：POM，请参见软管表C 13021。 Celcon® acetal copolymer grade M140 is a moderately high flow general purpose injection molding grade. It is designed for use in applications requiring some enhanced flow characteristics over the standard Celcon® M90 material. Chemical abbreviation according to ISO 1043-1: POM Please also see Hostaform® C 13021. |
产品描述 Product Description
用途：通用;
加工条件：注射成型 Injection Molding
性能特点： 流动性高; 易流动; High liquidity,Good liquidity
| 技术参数 Technical Data | |||
|---|---|---|---|
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
2740 | MPa | ISO 527-2/1A/1 |
|
拉伸强度 tensile strength |
ASTM D638 | ||
|
屈服 yield |
65.0 | MPa | ISO 527-2/1A/50 |
|
屈服，-40℃ Yield, -40 ℃ |
94.5 | MPa | ASTM D638 |
|
屈服，23℃ Yield, 23 ℃ |
60.7 | MPa | ASTM D638 |
|
屈服，71℃ Yield, 71 ℃ |
34.5 | MPa | ASTM D638 |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ISO 527-2/1A/50 | |
|
Tensile Creep Modulus（1 hr） Tensile Creep Modulus（1 hr） |
MPa | ISO 899-1 | |
|
拉伸蠕变模量 Tensile creep modulus |
|||
|
1000 hr 1000 hr |
MPa | ISO 899-1 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
1/℃ | ISO 11359-2 | |
|
MD MD |
1/℃ | ISO 11359-2 | |
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
g/cm³ | ASTM D792 | |
|
密度 Density |
g/cm³ | ISO 1183 | |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
190℃，2.16 kg 190℃，2.16 kg |
cm³/10min | ISO 1133 | |
|
收缩率 Shrinkage rate |
ISO 294-4 | ||
|
TD TD |
% | ASTM D955 | |
|
MD MD |
% | ASTM D955 | |
|
TD TD |
% | ISO 294-4 | |
|
MD MD |
% | ISO 294-4 | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
Density of Melt Density of Melt |
g/cm³ | Internal Method | |
|
Specific Heat Capacity of Melt Specific Heat Capacity of Melt |
J/kg/℃ | Internal Method | |
|
Thermal Conductivity of Melt Thermal Conductivity of Melt |
W/m/K | Internal Method | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 10°C/min |
|
【新闻资讯】查看全部 
耐克称新型发泡底可添加13%的反弹力
2018-01-31 耐克已经开始将其最为耐用和高反弹力的新型发泡底材料应用到跑鞋产品中，这款flyknit跑鞋2017年2月底已上市。 经过2000小时的测试，2017年6月耐克推出高反弹发泡缓冲篮球鞋。在其研发过程中，耐克 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |