POM共聚，Celcon® M140对比POM共聚，Hostaform® C 13021 LS物性表,价格行情_搜料

牌号信息	Celcon® M140 物性表 POM共聚 & 美国塞拉尼斯指导价格：暂无塑料库存：缺货	Hostaform® C 13021 LS 物性表 POM共聚 & 美国塞拉尼斯指导价格：暂无塑料库存：缺货
牌号简介	CELCON缩醛共聚物M140级是中等高流动性通用注射成型级。它设计用于需要在标准Celcon M90材料上增强流动特性的应用中。符合ISO 1043-1的化学缩写：POM，请参见软管表C 13021。 Celcon® acetal copolymer grade M140 is a moderately high flow general purpose injection molding grade. It is designed for use in applications requiring some enhanced flow characteristics over the standard Celcon® M90 material. Chemical abbreviation according to ISO 1043-1: POM Please also see Hostaform® C 13021.	POM共聚物易流动注射成型型，适用于高刚性、高硬度、高韧性的精密成型件和薄壁成型件；耐溶剂、燃料、强碱性好，耐水解性好；耐高温氧化降解。如果厚度超过1 mm，紫外线添加剂的燃烧速率为ISO 3795和FMVSS 302<75 mm/min。应用范围：汽车工程，精密工程，电工电子工业，家用电器。联邦机动车辆安全标准（美国） POM copolymer Easy flowing Injection molding type for precision molded parts and thin-walled molded parts with high rigidity, hardness and toughness; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. With UV Additives Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm. Ranges of applications: automotive engineering, precision engineering, electric and electronical industry, domestic appliances. FMVSS = Federal Motor Vehicle Safety Standard (USA)

产品描述
厂家：	美国塞拉尼斯 Celanese	美国塞拉尼斯 Celanese
类别：	POM共聚 Copolymer Polyformaldehyde	POM共聚 Copolymer Polyformaldehyde
填料：
用途：	通用	电器用具,汽车领域的应用,薄壁部件,电气/电子应用领域
性能特点：	流动性高,易流动 High liquidity,Good liquidity	机械强度好,耐候抗UV,韧性好,耐碱,耐水解,易流动,硬度高,耐化学性,耐燃油,防火阻燃等级HB Good Rigidity,Weather resistance is good,Good flexibility,Alkali resistant,Hydrolysis stability,Good liquidity,Good Hardness,Solvent resistance,Fuel resistance,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

机械性能
MECHANICAL Celcon® M140 Hostaform® C 13021 LS 单位
UNIT 测试方法
TEST METHOD

Tensile Creep Modulus(1 hr)
Tensile Creep Modulus（1 hr） MPa ISO 899-1

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2/1A/50

拉伸强度(屈服)
tensile strength MPa ISO 527-2/1A/50

拉伸强度(屈服，-40℃)
tensile strength MPa ASTM D638

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(屈服，71℃)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

拉伸蠕变模量(1000 hr)
Tensile creep modulus MPa ISO 899-1

标称拉伸断裂应变
Nominal tensile fracture strain % ISO 527-2/1A/50

冲击性能
IMPACT Celcon® M140 Hostaform® C 13021 LS 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Celcon® M140 Hostaform® C 13021 LS 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

物理性能
PHYSICAL Celcon® M140 Hostaform® C 13021 LS 单位
UNIT 测试方法
TEST METHOD

Density of Melt
Density of Melt g/cm³ Internal Method

Specific Heat Capacity of Melt
Specific Heat Capacity of Melt J/kg/℃ Internal Method

Thermal Conductivity of Melt
Thermal Conductivity of Melt W/m/K Internal Method

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ASTM D955

收缩率(TD)
Shrinkage rate % ISO 294-4

熔体体积流动速率(190℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

电气性能
ELECTRICAL Celcon® M140 Hostaform® C 13021 LS 单位
UNIT 测试方法
TEST METHOD

介电强度
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm IEC 60093

相对电容率(1 MHz)
Relative permittivity IEC 60250

相对电容率(100 Hz)
Relative permittivity IEC 60250

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

耗散因数(1 MHz)
Dissipation factor IEC 60250

耗散因数(100 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Celcon® M140 Hostaform® C 13021 LS 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

加工方式

注射 Celcon® M140 Hostaform® C 13021 LS 单位测试方法

保压 MPa

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

顶出温度 °C

备注

1 一般属性：这些不能被视为规格。

2 10°C/min

1 一般属性：这些不能被视为规格。

2 10°C/min


相关资讯

牌号简介
产品描述
技术参数
机械性能
冲击性能
热性能
物理性能
电气性能
阻燃性能
加工方式
注射
备注
返回顶部

POM共聚，Celcon® M140对比POM共聚，Hostaform® C 13021 LS对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别