Lubrione润滑和耐磨化合物被专门配制成自润滑材料,提供低摩擦系数和改进的耐磨性能。润滑油化合物已被证明可以减少摩擦、噪音、振动、热积聚并提高产品的耐久性。 MAJ'ECO EN000LA is a bio polymer material intended for injection moulding. MAJ'ECO EN000LA has been developed especially for demanding applications in various engineering sectors. APPLICATIONS Product such as: Boxes Racks Technical components |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.25 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
15 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
4.0E-3 | % | 内部方法 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弹性模量 Elastic modulus 2 |
|||
MD MD 2 |
3500 | MPa | ASTM D882 |
拉伸强度 tensile strength 3 |
|||
MD,断裂 MD, fracture 3 |
52.0 | MPa | ASTM D882 |
MD,屈服 MD, yield 3 |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 3 |
|||
MD,断裂 MD, fracture 3 |
% | ASTM D882 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
高桥石化聚醚装置技术改进 危废物大幅增加
2016-05-10 高桥石化聚醚装置加强源头治理和精细管理,从2013年起,废危物呈两位数的速率下降,目前,整个装置废危物比2013年减少三分之二。 聚醚装置于2013年建立由作业部部长挂帅,装置长和各专业组组长、科研骨干组成的攻关小组,研究减废工作现状、改进手段,确保废危物减量化年年有进步。 过去取样实施敞开式人工作业,一些取出的物料中会进入灰尘导致废液产生或需要重新加工。装置取样点众多,年积月累,形成了一定的废危物量。 回收利用时小桶倒大桶,容易掉落物料,成 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |