牌号简介 About |
---|
Techno-Cote by Clear Cote是一个3速(2到1,按体积/重量计算)高质量的层压系统。它是100%环氧固体。适用于玻璃纤维、芳纶、碳纤维等复合材料的快速浸润。根据所需的固化速度和使用寿命,该系统可与3种不同活化剂中的任何一种一起购买。该材料具有易于使用的2:1混合比(2份树脂与1份活化剂,按体积/重量计),在室温下固化,几乎不脸红,形成坚硬、抗冲击的塑料,具有优异的耐水性、耐化学品性和耐溶剂性。这种材料适用于机械容积泵,一定要充分混合这些材料,并确保刮掉侧面和底部。与所有粘合剂类型的化合物一样,适当的表面处理对于良好的粘合强度至关重要,此外,应在材料彻底固化之前完成该材料的重新涂层,一般不超过24小时。如果材料已硬化且无粘性,则在重新涂层之前需要进行砂光和溶剂清洗。 TECHNO-COTE™ by CLEAR COTE™ is a 3 Speed (2 to 1, by volume/weight ) high quality, laminating system. It is 100% Epoxy solids. It is designed for the rapid wet out of fiberglass, Kevlar, carbon fiber and other composite materials. This system can be purchased with any one of 3 different Activators depending up on the desired cure speed and pot life. The material has an easy to use 2 to 1 mix ratio (2 Parts resin to 1 Part Activator, by volume/weight ) that cures at room temperature with little to no blush to a tough, rigid, impact resistant plastic, with excellent resistance to water, chemicals, and solvents. This material is suitable for use in mechanical volume pumps, always mix these materials thoroughly and be sure to scrape the sides and bottom. As with all adhesive type compounds proper surface preparation is essential for good bond strength, additionally recoating of this material should be accomplished before the material is thoroughly cured generally in less then 24 hours. If the material has cured hard and tack free, a sanding and solvent wash will be necessary before recoating. |
技术参数 Technical Data | |||
---|---|---|---|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
工作温度 working temperature |
|||
慢活化剂 Slow activator 2 |
-40 到 66 | ℃ | |
中型活化剂 Medium size activator 3 |
-40 到 66 | ℃ | |
快速活化剂 Rapid activator 4 |
-40 到 66 | ℃ | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
慢活化剂 Slow activator 2 |
琥珀色 | ||
中型活化剂 Medium size activator 3 |
琥珀色 | ||
快速活化剂 Rapid activator 4 |
|||
层压树脂 Laminated resin 5 |
|||
粘度 viscosity |
|||
慢活化剂 Slow activator 2 |
Pa·s | ||
中型活化剂 Medium size activator 3 |
Pa·s | ||
快速活化剂 Rapid activator 4 |
Pa·s | ||
层压树脂 Laminated resin 5 |
Pa·s | ||
胶凝时间 Gelation time |
|||
25℃ 25℃ 4 |
min | ||
25℃ 25℃ 3 |
min | ||
25℃ 25℃ 2 |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D 2 |
|||
拉伸应变 Tensile strain |
|||
断裂,快速激活剂 Fracture, rapid activator 4 |
% | ||
断裂,中型活化剂 Fracture, medium activator 3 |
% | ||
断裂,慢活化剂 Fracture, slow activator 2 |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
慢活化剂 Slow activator 2 |
℃ | ||
中型活化剂 Medium size activator 3 |
℃ | ||
快速活化剂 Rapid activator 4 |
℃ | ||
热固组件 Thermosetting components |
|||
部件 C Component C 4 |
|||
部件 A Component A 2 |
|||
部件 B Component B 3 |
|||
树脂 resin |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
镇海炼化借力塑胶会平台推行新产品
2017-10-24 2017年10月12-15日,中国塑料交易会在浙江台州举行。镇海炼化生产的快速成型聚丙烯M60ET新产品受到众多企业代表的关注。 中国塑料交易会是中国塑料行业重要展会之一,成为全面展示塑料产业状况的窗口,设立原料、机械、模具、制品四大展馆。台州是中国最大的塑料生产基地,是塑料产业终端核心区,聚烯烃加工企业众多,是公司聚烯烃产品销售的重点地区。镇海炼化开发的M60ET属于环保型新产品,因其良好的流动性能及优异的透明性能,广泛应用于高端包装、食品容器、日用品等领域。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |