牌号简介 About |
---|
EpoxAcast® 655(原名metalset A-30)是一种多功能的铝填充可浇铸环氧树脂,非常坚硬和坚固。它在尺寸上是稳定的,即使质量在3/8390 cm 3中达到512。根据您的项目要求,可提供不同的硬化剂速度选项。使用高温硬化剂(最高225°F/108°C)可达到最大耐热性。固化EpoxAcast® 655环氧树脂具有高物理性能,可用于各种应用,包括制造硬工具、真空成型模具/模具、注射模具、铸造模式、夹具和夹具以及金属成型模具。根据项目要求,A部分基础可与101快、102中、103慢或高温硬化剂混合。 EpoxAcast® 655 (formerly Metalset® A-30) is a versatile aluminum filled castable epoxy that is very hard and strong. It is dimensionally stable, even when mass cast up to 512 in 3 / 8,390 cm 3. Different hardener speed options are available depending on your project requirements. Maximum heat resistance is achieved using HT HIGH TEMP hardener (up to 225°F/108°C). Cured EpoxAcast® 655 epoxy has high physical properties and is used for a variety of applications including making hard tooling, vacuum forming dies/molds, injection molds, foundry patterns, jigs and fixtures and metal forming dies. Depending on project requirements, Part A Base can be mixed with 101 FAST, 102 MEDIUM, 103 SLOW or HT HIGH TEMP hardeners. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
ASTM D1475 | ||
-- -- 2 |
1.64 | g/cm³ | ASTM D1475 |
-- -- 3 |
1.66 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
ASTM D792 | ||
-- -- 3 |
0.603 | cm³/g | ASTM D792 |
-- -- 2 |
0.596 | cm³/g | ASTM D792 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength |
24.5 | kN/m | ASTM D624 |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
-- -- 3 |
cP | ||
-- -- 2 |
cP | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
23℃ 23℃ 6 |
hr | ||
23℃ 23℃ 7 |
hr | ||
23℃ 23℃ 8 |
hr | ||
66℃ 66℃ 6 |
hr | ||
66℃ 66℃ 7 |
hr | ||
66℃ 66℃ 8 |
hr | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness 3 |
|||
邵氏 D Shaw's D 3 |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
ASTM D638 | ||
-- -- 3 |
MPa | ASTM D638 | |
-- -- 2 |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ASTM D638 | ||
断裂 fracture 2 |
MPa | ASTM D638 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂 fracture 2 |
% | ASTM D638 | |
断裂 fracture 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
ASTM D695 | ||
-- -- 3 |
MPa | ASTM D695 | |
-- -- 2 |
MPa | ASTM D695 | |
压缩强度 compressive strength |
ASTM D695 | ||
-- -- 3 |
MPa | ASTM D695 | |
-- -- 2 |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed 4 |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed 5 |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
部件 A Component A 8 |
|||
部件 B Component B 6 |
|||
部件 B Component B 7 |
|||
部件 B Component B 8 |
|||
部件 B Component B 9 |
|||
储存稳定性 storage stability |
|||
23℃ 23℃ 6 |
min | ||
23℃ 23℃ 7 |
min | ||
23℃ 23℃ 8 |
min | ||
23℃ 23℃ 9 |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Using HT Hardner |
3 Using 101, 102 or 103 Hardner |
4 Using HT Hardner, if post cured according to post curing schedule |
5 Using 101, 102 or 103 Hardner, If cured at room temperature |
6 HT HIGH TEMP Hardener |
7 103 SLOW Hardener |
8 102 MEDIUM Hardener |
9 101 FAST Hardener |
10 HT HIGH TEMP Hardener, followed by 2 hr at 175°F and 3 hr at 300°F |
【新闻资讯】查看全部
国务院发布一则“无废城市”建立试点任务方案
2019-02-11 近日,国务院发布的一则 “无废城市”建设试点工作方案(以下简称《方案》)轰轰轰地上了微博热搜。 《方案》指出,今年将在全国范围内选择10个左右有条件、有基础、规模适当的城市,开展“无废城市”建设试点。计划到2020年,形成一批可复制、可推广的“无废城市”建设示范模式。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |