牌号简介 About |
---|
MVR(300°C/1.2 kg)9.0 cm³/10 min;阻燃剂;UL 94V-0/1.5 mm和5VA/3.0 mm;中等粘度;易释放;注射成型-熔融温度280-320°C;仅提供不透明颜色 MVR (300 °C/1.2 kg) 9.0 cm³/10 min; flame retardant; UL 94V-0/1.5 mm and 5VA/3.0 mm; medium viscosity; easy release; injection molding - melt temperature 280 - 320 °C; available in opaque colors only |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.64 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
9.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD TD |
0.60 to 0.80 | % | ISO 2577 |
MD MD |
% | ISO 2577 | |
TD:2.0 mm TD:2.0 mm |
% | ISO 294-4 | |
MD:2.0 mm MD:2.0 mm |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 7391 | ||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 7391 | |
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ISO 7391 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-60℃ -60℃ |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 7391 | ||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 7391 | |
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ISO 7391 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
-30℃ -30℃ |
J | ISO 6603-2 | |
23℃ 23℃ |
J | ISO 6603-2 | |
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
ISO 6603-2 | ||
-30℃ -30℃ |
N | ISO 6603-2 | |
23℃ 23℃ |
N | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357-2 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
136℃ 136℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
|||
23℃ 23℃ |
W/m/K | ISO 8302 | |
相对温度指数 Relative temperature index |
|||
电气性能,1.50 mm Electrical performance, 1.50 mm |
℃ | UL 746 | |
强度机械性能,1.50 mm Strength mechanical performance, 1.50 mm |
℃ | UL 746 | |
冲击机械性能,1.50 mm Impact mechanical performance, 1.50 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
解决方案 A Solution A |
V | IEC 60112 | |
解决方案 B Solution B |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
小型燃烧器火焰的应用 The Application of Small Burner Flames |
|||
Method K and F,2.00 mm Method K and F,2.00 mm |
DIN 53438-1, -3 | ||
燃烧速率 Burning rate |
|||
USFMVSS,> 1.00 mm USFMVSS,> 1.00 mm |
ISO 3795 | ||
Flash Ignition Temperature Flash Ignition Temperature |
℃ | ASTM D1929 | |
Glow Wire Test Glow Wire Test |
EDF HN60 E.02 | ||
1.50 mm 1.50 mm |
℃ | EDF HN60 E.02 | |
3.00 mm 3.00 mm |
℃ | EDF HN60 E.02 | |
针焰测试 Needle flame test |
IEC 60695-11-5 | ||
Method F:1.50 mm Method F:1.50 mm |
min | IEC 60695-11-5 | |
Method F:2.00 mm Method F:2.00 mm |
min | IEC 60695-11-5 | |
Method F:3.00 mm Method F:3.00 mm |
min | IEC 60695-11-5 | |
Method K:1.50 mm Method K:1.50 mm |
min | IEC 60695-11-5 | |
Method K:2.00 mm Method K:2.00 mm |
min | IEC 60695-11-5 | |
Method K:3.00 mm Method K:3.00 mm |
min | IEC 60695-11-5 | |
自燃温度 Autoignition temperature |
℃ | ASTM D1929 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
|||
23℃ 23℃ |
IEC 60426 | ||
ISO Shortname ISO Shortname |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/50 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/50 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2/50 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Bending strain |
% | ISO 178 | |
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Pellets |
3 60x60x2 mm, 500 bar |
4 0.079 in/min |
5 2 mm/min |
6 Based on ISO 179-1eA, 3 mm |
7 Based on ISO 180-A, 3 mm |
8 10°C/min |
9 Cross-flow |
10 程序 A |
【新闻资讯】查看全部
深圳机械行业协会组织共探工业级3D打印技术
2016-07-14 7月12日,深圳机械行业协会智能制造众创空间联合深圳机械展,特邀日本OPM研究所、(株)松井制造所、Moldex3D台湾科盛、开思网,以日系3D打印――复合型金属3D打印机为背景,讨论3D打印在注塑模具上的优势与案例分析。 |
深圳机械行业协会组织共探工业级3D打印技术 7月12日,深圳市机械设备产业协会智能制造系统创客空间协同深圳机械展,特聘日本OPM研究室、(株)松井生产制造所、Moldex三维中国台湾科盛、开思网,以日式三维打印――复合性金属材料三维打印机为情况,探讨三维打印在塑料模具上的优点与经典案例。 此次大会以模具制造企业为目标,致力于引进新式生产加工技术性,推动模具制造生产制造行业发展。该类适用型活动备受企业热烈欢迎,在本来只有容下70人的大型会议室内观众总人数超出了100人,许多企业意味着加座在门口听完后全部大会演说。深机协副理事长姚纪广简洁明了详细介绍了研究会现阶段现有的各类综合服务平台,并提到研究会事后将再次多机构该类好用、能落地式的技术专业主题活动,为企业生产制造出示进一步的协助。 深机协智能制造系统创客空间众创空间项目经理、开思网经理金欣详细介绍了三维打印云服务平台,三维打印云服务平台做为联络三维打印要求和三维打印服务提供商的公路桥梁,能为必须三维打印、手板模型试品的企业或是本人出示方便快捷式的成形服务项目,免除因订单信息量很小而找不着三维打印生产商的苦恼。 日本OPM &上海市立模激光器森本一穗院长、中国台湾松井国际性股权有限责任公司徐尉凯协理、中国台湾区电脑上輔助成形行业交流研究会蔡铭宏理事长各自共享了日本复合性金属材料三维打印技术性、翠绿色成形核心理念与异形水道模貝等运用实例、及其Moldex三维异形水道剖析与模貝溫度急冷急热精细分析。一个个符合实际的运用实例和解决方法为出席会议的模具制造企业产生了最前沿的三维打印技术性和新式生产加工技术性。 会议后,出席会议企业意味着们移景参观考察了研究会智能制造系统创客空间,并与智能制造系统创客空间责任人讨论了众创空间新项目的运行体制和步骤。 来源于:中塑在线原創 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。