牌号简介 About |
---|
PBT,非增强,挤压,食品接触 POCAN® B1701 000000 PBT, non-reinforced, extrusion, suitable for food-contact POCAN® B1701 000000 PBT, non-reinforced, extrusion, suitable for food-contact POCAN® B1701 000000 PBT, non-reinforced, extrusion, suitable for food-contact |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.31 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.80 | g/cm³ | ISO 60 |
熔体体积流动速率 Melt Volume Rate |
|||
250℃,2.16 kg 250℃,2.16 kg |
8.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage |
ISO 2577 | ||
TD:260℃,2.0 mm TD:260℃,2.0 mm |
2.0 | % | ISO 2577 |
TD:120℃,2.0 mm,4 hrs TD:120℃,2.0 mm,4 hrs |
0.20 | % | ISO 2577 |
MD:260℃,2.0 mm MD:260℃,2.0 mm |
% | ISO 2577 | |
MD:120℃,2.0 mm,4 hrs MD:120℃,2.0 mm,4 hrs |
% | ISO 2577 | |
吸水率 Water Absorption |
ISO 62 | ||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2/50 | |
弯曲模量 Flexural Modulus |
|||
23℃ 23℃ |
MPa | ISO 178-A | |
弯曲强度 Flexural Strength |
ISO 178/A | ||
23℃ 23℃ |
MPa | ISO 178-A | |
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178-A | |
弯曲应变 Flexural Strain |
% | ISO 178/A | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Izod Notched Impact strength |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temperature |
|||
B120 B120 |
℃ | ISO 306/B120 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Coeff.of linear therm expansion |
ISO 11359-2 | ||
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Comparative Tracking Index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
ISO 7792 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2mm, 80°C MT, 600 bar |
3 60x60x2mm |
4 0.079 in/min |
5 2 mm/min |
6 10°C/min |
【新闻资讯】查看全部 ![]()
清点包装用塑料薄膜的功能要求
2015-12-03 包装用塑料薄膜需具备以下特性: 一、良好的阻隔性 包装用塑料薄膜应该具有良好的阻隔性,以防止氧气、水蒸汽相液体的渗透。作为食品包装用薄膜,一般要求能够阻隔氧气和细菌,以便能延长保质期。对于肉类、巧克力和饼干等的包装薄膜,对水蒸汽的阻隔性要求很高,因为肉类和巧克力若失水会变干,而饼干若吸水则易变质。此外,包装金属零件的薄膜,应该能够阻隔氧气和水蒸汽,因为金属零件发生诱蚀的条件是氧气相水并存。苦通的LDPE薄膜能够透过氧气和水蒸汽,如果要用于阻隔性包装,就必须与 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |