PBT，Durethan® B 1701 00000对比PBT，POCAN® B 1700 000000物性表,价格行情_搜料

牌号信息	Durethan® B 1701 00000 物性表 PBT & 德国恩骅力指导价格：暂无塑料库存：缺货	POCAN® B 1700 000000 物性表 PBT & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	PBT，非增强，挤压，食品接触 POCAN® B1701 000000 PBT, non-reinforced, extrusion, suitable for food-contact POCAN® B1701 000000 PBT, non-reinforced, extrusion, suitable for food-contact POCAN® B1701 000000 PBT, non-reinforced, extrusion, suitable for food-contact	Pocan B 170000000 PBT，非增强，挤压，食品接触 POCAN® B1700 000000 PBT, non-reinforced, extrusion, suitable for food-contact POCAN® B1700 000000 PBT, non-reinforced, extrusion, suitable for food-contact POCAN® B1700 000000 PBT, non-reinforced, extrusion, suitable for food-contact

产品描述
厂家：	德国恩骅力 Envalior	德国恩骅力 Envalior
类别：	PBT polybutylene terephthalate	PBT polybutylene terephthalate
填料：
用途：
性能特点：	防火阻燃等级HB,食品接触 HB,Food contact compliance	食品接触,防火阻燃等级HB Food contact compliance,HB
加工条件：	挤出 Extrusion	挤出 Extrusion

技术参数

物理性能
PHYSICAL Durethan® B 1701 00000 POCAN® B 1700 000000 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(MD：120℃，2.0 mm，4 hrs)
Shrinkage rate % ISO 2577

收缩率(MD：150℃，3.0 mm，1 hrs)
Shrinkage rate % ISO 2577

收缩率(MD：260℃，2.0 mm)
Shrinkage rate % ISO 2577

收缩率(MD：260℃，3.0 mm)
Shrinkage rate % ISO 2577

收缩率(TD：120℃，2.0 mm，4 hrs)
Shrinkage rate % ISO 2577

收缩率(TD：150℃，3.0 mm，1 hrs)
Shrinkage rate % ISO 2577

收缩率(TD：260℃，2.0 mm)
Shrinkage rate % ISO 2577

收缩率(TD：260℃，3.0 mm)
Shrinkage rate % ISO 2577

熔体体积流动速率(250℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

粘度值(降低的粘度)
Viscosity value ml/g ISO 1628

表观密度
Apparent density g/cm³ ISO 60

机械性能
MECHANICAL Durethan® B 1701 00000 POCAN® B 1700 000000 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain % ISO 178/A

弯曲强度(23℃)
bending strength MPa ISO 178-A

弯曲强度(3.50% 应变，23℃)
bending strength MPa ISO 178-A

弯曲模量(23℃)
Bending modulus MPa ISO 178-A

拉伸应变(屈服，23℃)
Tensile strain % ISO 527-2/50

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2/50

拉伸模量(23℃)
Tensile modulus MPa ISO 527-1-2

标称拉伸断裂应变(23℃)
Nominal tensile fracture strain % ISO 527-2/50

冲击性能
IMPACT Durethan® B 1701 00000 POCAN® B 1700 000000 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击力峰值(-30℃)
Multi axial instrumented peak impact force N ISO 6603-2

多轴向仪器化冲击力峰值(23℃)
Multi axial instrumented peak impact force N ISO 6603-2

多轴向仪器化冲击能量(-30℃)
Multi axial instrumented impact energy J ISO 6603-2

多轴向仪器化冲击能量(23℃)
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Durethan® B 1701 00000 POCAN® B 1700 000000 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(8.0 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/C

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

电气性能
ELECTRICAL Durethan® B 1701 00000 POCAN® B 1700 000000 单位
UNIT 测试方法
TEST METHOD

介电强度(23 ℃，1 mm)
Dielectric strength kV/mm IEC 60243-1

体积电阻率(23℃)
Volume resistivity ohms·cm IEC 60093

相对电容率(23℃，1 MHz)
Relative permittivity IEC 60250

相对电容率(23℃，100 Hz)
Relative permittivity IEC 60250

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

耗散因数(23℃，1 MHz)
Dissipation factor IEC 60250

耗散因数(23℃，100 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Durethan® B 1701 00000 POCAN® B 1700 000000 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.80 mm)
Flame retardant level UL 94

阻燃等级(1.60 mm)
Flame retardant level UL 94

补充信息
Durethan® B 1701 00000 POCAN® B 1700 000000 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname ISO 7792

加工方式

注射 Durethan® B 1701 00000 POCAN® B 1700 000000 单位测试方法

Residual Moisture Content %

干燥时间 - 除湿干燥剂 hr

干燥温度 - 除湿干燥剂 °C

备注

1 一般属性：这些不能被视为规格。

2 60x60x2mm, 80°C MT, 600 bar

3 60x60x2mm

4 0.079 in/min

5 2 mm/min

6 10°C/min

1 一般属性：这些不能被视为规格。

2 150x105x3mm, 80°C MT, 600 bar

3 150x105x3mm

4 0.079 in/min

5 2 mm/min

6 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
备注