牌号简介 About |
---|
Eastapak Polymer 9921是一种0.80 ltv(dl/g)共聚物PET,已被证明是一种特殊的、具有成本效益的选择,在广泛的应用中继续超越对质量、效率和便利性的期望。 Eastapak™ Polymer 9921 is an 0.80 ltV (dL/g) copolymer PET that has proven itself as an exceptional, cost-effective option that continues to surpass expectations for quality, efficiency and convenience in a wide array applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.33 | g/cm³ | ASTM D792 |
285℃ 285℃ |
1.10 | g/cm³ | ISO 1183/A |
-- -- |
1.40 | g/cm³ | ASTM D1505 |
表观密度 Apparent density |
ASTM D1895 | ||
-- -- 3 |
0.85 | g/cm³ | ASTM D1895 |
-- -- 4 |
0.91 | g/cm³ | ASTM D1895 |
固有粘度 Intrinsic viscosity 5 |
|||
23℃ 23℃ 5 |
|||
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
割线模量 Secant modulus |
ASTM D882 | ||
MD:260 µm MD:260 µm |
MPa | ASTM D882 | |
TD:260 µm TD:260 µm |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,260 µm MD, yield, 260 µ m |
MPa | ASTM D882 | |
TD,屈服,260 µm TD, yield, 260 µ m |
MPa | ASTM D882 | |
MD,断裂,260 µm MD, fracture, 260 µ m |
MPa | ASTM D882 | |
TD,断裂,260 µm TD, fracture, 260 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,屈服,260 µm MD, yield, 260 µ m |
% | ASTM D882 | |
TD,屈服,260 µm TD, yield, 260 µ m |
% | ASTM D882 | |
MD,断裂,260 µm MD, fracture, 260 µ m |
% | ASTM D882 | |
TD,断裂,260 µm TD, fracture, 260 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 6 |
ASTM D1709A | ||
-18℃,260 µm -18℃,260 µm |
g | ASTM D1709-A | |
23℃,260 µm 23℃,260 µm |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:260 µm MD:260 µm |
g | ASTM D1922 | |
TD:260 µm TD:260 µm |
g | ASTM D1922 | |
裤型撕裂耐性 Pant tear resistance 7 |
ISO 6383-1 | ||
MD:260 µm MD:260 µm |
N/mm | ISO 6383-1 | |
TD:260 µm TD:260 µm |
N/mm | ISO 6383-1 | |
透氧率 Oxygen permeability |
|||
30℃,250 µm,50% RH 30℃,250 µm,50% RH |
cm³·mm/m²/atm/24 hr | ASTM D3985 | |
水蒸气透过性 Water vapor permeability |
g/m²/24 hr | ASTM E96 | |
二氧化碳渗透性 Carbon dioxide permeability |
|||
23℃,260.0 µm 23℃,260.0 µm |
cm³·mm/m²/atm/24 hr | ASTM D1434 | |
PPT撕裂阻力 PPT tear resistance |
ASTM D2582 | ||
MD:23℃,260.0 µm MD:23℃,260.0 µm |
N | ASTM D2582 | |
TD:23℃,260.0 µm TD:23℃,260.0 µm |
N | ASTM D2582 | |
抗撕裂蔓延性 Tear resistant vine ductility 8 |
ASTM D1938 | ||
MD:23℃,260.0 µm MD:23℃,260.0 µm |
kN/m | ASTM D1938 | |
TD:23℃,260.0 µm TD:23℃,260.0 µm |
kN/m | ASTM D1938 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-40℃,注塑成型 -40 ℃, injection molding |
J/m | ASTM D256 | |
23℃,注塑成型 23 ℃, injection molding |
J/m | ASTM D256 | |
-40℃,注塑成型 -40 ℃, injection molding |
kJ/m² | ISO 180-1A | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-40℃,3.2 mm,注塑成型 -40 ℃, 3.2 mm, injection molding |
J/m | ASTM D4812 | |
-30℃,3.2 mm,注塑成型 -30 ℃, 3.2 mm, injection molding |
ASTM D4812 | ||
-20℃,3.2 mm,注塑成型 -20 ℃, 3.2 mm, injection molding |
ASTM D4812 | ||
23℃,3.2 mm,注塑成型 23 ℃, 3.2 mm, injection molding |
ASTM D4812 | ||
-40℃,注塑成型 -40 ℃, injection molding 9 |
kJ/m² | ISO 180/1U | |
-30℃,注塑成型 -30 ℃, injection molding 9 |
kJ/m² | ISO 180/1U | |
-20℃,注塑成型 -20 ℃, injection molding 9 |
ISO 180/1U | ||
23℃,注塑成型 23 ℃, injection molding 9 |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
-40℃,2.50 mm,注塑,Energy to Max Load -40 ℃, 2.50 mm, injection molded, Energy to Max Load |
J | ASTM D3763 | |
-40℃,3.20 mm,注塑,Energy to Max Load -40 ℃, 3.20 mm, injection molded, Energy to Max Load |
J | ASTM D3763 | |
23℃,2.50 mm,注塑,Energy to Max Load 23 ℃, 2.50 mm, injection molded, Energy to Max Load |
J | ASTM D3763 | |
23℃,3.20 mm,注塑,Energy to Max Load 23 ℃, 3.20 mm, injection molded, Energy to Max Load |
J | ASTM D3763 | |
-40℃,2.50 mm,注塑,能量到力量峰值 -40 ℃, 2.50 mm, injection molding, energy to peak force 10 , 11 |
J | ISO 6603-2 | |
-40℃,3.20 mm,注塑,能量到力量峰值 -40 ℃, 3.20 mm, injection molding, energy to peak force 10 , 11 |
J | ISO 6603-2 | |
23℃,2.50 mm,注塑,能量到力量峰值 23 ℃, 2.50 mm, injection molding, energy to peak force 10 , 11 |
J | ISO 6603-2 | |
23℃,3.20 mm,注塑,能量到力量峰值 23 ℃, 3.20 mm, injection molding, energy to peak force 10 , 11 |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,注塑成型 0.45 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火,注塑 1.8 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
结晶峰温度 Crystallization peak temperature 12 |
|||
DSC DSC 12 |
℃ | ASTM D3418 | |
比热 specific heat 13 |
ASTM C351 | ||
23℃ 23℃ |
J/kg/℃ | ASTM C351 | |
80℃ 80℃ |
J/kg/℃ | ASTM C351 | |
100℃ 100℃ |
J/kg/℃ | ASTM C351 | |
200℃ 200℃ |
J/kg/℃ | ASTM C351 | |
280℃ 280℃ |
J/kg/℃ | ASTM C351 | |
融合热量 Fusion heat 13 |
|||
23℃ 23℃ 13 |
kJ/kg | ASTM E793 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,264 µm 60°,264 µm |
ASTM D2457 | ||
透光率 Transmittance |
ASTM D1003 | ||
常规,264 µm Regular, 264 µ m |
% | ASTM D1003 | |
总计,264 µm Total, 264 µ m |
% | ASTM D1003 | |
透明度 transparency |
|||
264 µm 264 µm |
ASTM D1746 | ||
雾度 Haze |
|||
264 µm 264 µm |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颗粒形状 Particle shape |
|||
颗粒大小 Particle size |
mm | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级,23℃,注塑成型 R-grade, 23 ℃, injection molding |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
23℃,注塑成型 23 ℃, injection molding |
MPa | ASTM D638 | |
23℃,注塑成型 23 ℃, injection molding |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃,注塑成型 Yield, 23 ℃, injection molding |
MPa | ASTM D638 | |
屈服,23℃,注塑成型 Yield, 23 ℃, injection molding |
MPa | ISO 527-2 | |
断裂,23℃,注塑成型 Fracture, 23 ℃, injection molding |
MPa | ASTM D638 | |
断裂,23℃,注塑成型 Fracture, 23 ℃, injection molding |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃,注塑成型 23 ℃, injection molding |
MPa | ASTM D790 | |
23℃,注塑成型 23 ℃, injection molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃,注塑成型 23 ℃, injection molding |
MPa | ISO 178 | |
屈服,23℃,注塑成型 Yield, 23 ℃, injection molding |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Vibrated |
3 Poured |
4 EMN-A-AC-G-V-1 |
5 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
6 7.9 in/min |
7 @ 254 mm/min |
8 4 mm |
9 13.5 ft/sec, 0.79 in 冲击器直径 |
10 40 mm support and clamp diameter |
11 Determined by DSC on the second heating cycle. Melting point rounded to the nearest 5°C because of variability of results. |
12 Determined by DSC on the first heating cycle. |
【新闻资讯】查看全部
三坐标测量机测量同轴度误差的正确办法
2016-09-19 同轴度是机械产品检测中比较常见的一种形位公差项目,其表示零件的有关要素(轴与轴、孔与孔、轴与孔之间)要求同轴,即控制实际轴线与基准轴线的偏离程度。对于那个规则轴类零件,一般可采用V型支架、钢球加杠杆百分表或偏摆仪等专用检具及组合辅具来检测同轴度;对于箱体孔类零件,一般可采用芯轴加杠杆百分表或利用圆度仪来检测同轴度。 但是对于一些大型零部件(如机床主轴等)或不规则轴类零件以及箱体零件的不规则内孔,采用常规方法测量同轴度则很难实现或非常麻烦。因此,使用三坐标测量机来测量同轴度是 |
三坐标测量机测量同轴度误差的正确办法 同轴度是机械设备产品质量检测中较为普遍的一种尺寸公差新项目,其表明零件的相关因素(轴与轴、孔与孔、轴与孔中间)规定同轴输出,即操纵具体轴线与基准轴线的偏移水平。针对哪个标准轴类零件,一般可选用V型支撑架、轴承钢球杠杆炒股内径百分表或偏摆仪等专用型工装夹具及组成辅具来检验同轴度;针对壳体孔类零件,一般可选用芯棒杠杆炒股内径百分表或运用圆度仪来检验同轴度。 可是针对一些大中型零部件(如车床主轴等)或不规律轴类零件及其壳体零件的不规律内螺纹,选用基本方式测量同轴度则难以完成或十分不便。因而,应用三坐标测量机来测量同轴度是一种非常好的挑选。与专用型同轴度测量仪对比,CMM测量同轴度的较大 特性是不必旋转产品工件,不必专用型芯棒或专用型支撑架,不必机械设备找正,只要用测头探头对产品工件采点取样,就可以迅速輸出测量結果。但用CMM测量同轴度时,因为对基准轴线了解的差别,或对被测因素轴线测量方式不一样,或对同轴度评价方法不一样,及其CMM采点误差的危害等缘故,有时候会出現测量結果误差很大、可重复性较弱的状况,即测量結果不可以真正体现零件真正的同轴度误差。 依据同轴度的界定,用三坐标测量机测量同轴度时,可从三个层面调查其测量误差:1.基准轴线的收集与创建;2.被测原素轴线的收集与创建;3.基准轴线与被测原素轴线中间位置关系的点评。而减少三坐标测量机测量同轴度误差的方式关键有以下好多个方式: 1.扩大基准截面中间的间距 在测量基准原素时,若扩大第一截面与第二截面建的间距,则误差影响的占比将相对减少。因而,测量时要尽量放大两截面间的间距。若基准充足长,且基准截面与被检截面邻近,则造成的误差可小到忽略。 2.创建公共性轴线做为基准轴线 当基准圆柱体和被测圆柱体较短且欢聚较远时,可选用创建公共性轴线做为基准轴线的方式,即在基准圆柱体和被测圆柱体上测到中截面,以中截面的相互连接做为公共性轴线,随后各自测算基准圆柱体和被测圆柱体相对性于公共性轴线(基准轴线)的同轴度,取其最高值做为产品工件的同轴度误差。该方式的点评結果较为结晶体具体应用状况。 3.以平行度类似取代同轴度 在被测产品工件截面较短的状况下,能用改测平行度以取代同轴度的变通方法。由于这类状况下轴的歪斜对产品工件安装危害较小,而枢轴偏位对产品工件安装危害很大,测量枢轴偏位事实上便是测量枢轴联线的平行度。具备完成方式为:各自在2个小圆柱体上测量n个截面圆,随后选择这n个圆的圆心点线性拟合一条三维平行线,该平行线的平行度可类似取代同轴度。工作中截面越少,该方式实际效果越好,而且可很便捷地制做一个综合性量规来认证该方式的精确性。 之上便是我们测量为大伙儿梳理的相关三坐标测量机测量同轴度误差的恰当方式有关专业知识,期待可以给大伙儿产生协助。我们做为世界最大的测量技术性集团公司海克斯康集团旗下的分公司之一,借助集团公司经济全球化的区位优势和顶级的技术性优点,我们商品有着最大性价比高,让用户体验进口商品的品质,国内商品的价钱。 来源于:我们测量 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。