牌号简介 About |
---|
Lexan ML6411树脂Lexan ML6411聚碳酸酯(PC)硅氧烷树脂,是一种高流动性不透明注塑成型(IM)级,具有极低的温度延性特性。该等级提供基于无氯、无溴阻燃系统的UL94V0@1.5mm和5VA@3.0mm阻燃性。与标准PC相比,LEXAN™ ML6411 resin具有出色的加工特性,有机会缩短IM周期。该产品有多种不透明颜色,是广泛电气应用的理想选择。 LEXAN ML6411 polycarbonate (PC) siloxane resin, is a high flow opaque injection molding (IM) grade with very low temperature ductility characteristics. This grade offers UL94 V0 @ 1.5mm and 5VA @ 3.0mm flame retardancy based on non-chlorine, non-bromine FR systems. LEXAN ML6411 resin offers excellent processing characteristics with opportunity for shorter IM cycle times compared to standard PC. This product is available in a wide range of opaque colors and is an excellent candidate for a wide range of electrical applications. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PC Polycarbonate
用途:电气/电子应用领域;
颜色:不透明
加工条件:注射成型 Injection Molding
性能特点: 无卤; 防火阻燃等级V-0; 成型周期快; 防火阻燃等级5VB; 机械强度好-延展; 流动性高; 阻燃; 防火阻燃等级5VA; 易加工; Excellent Processability,High liquidity,Ductility,Quick molding cycle,Halogen free,Flame Characteristics,V-0,5VA,5VB
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,2.16kg 260℃,2.16kg |
7.0 | g/10min | ASTM D1238 |
300℃,1.2kg 300℃,1.2kg |
15 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,5 kg 260℃,5 kg |
18.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture |
MPa | ASTM D638 | |
屈服 yield |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
50 mm跨距 50 mm span |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
屈服,50 mm跨度 Yield, 50 mm span |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span |
℃ | ISO 75-2/Ae | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,100 mm跨距 0.45 MPa, unannealed, 100 mm span |
℃ | ISO 75-2/Be | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 9 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
2.00 mm 2.00 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*3 |
8 120*10*4 mm |
9 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
科鲁尔公司 丙烯腈工程开车成功
2021-11-12 搜料网资讯: 10月底,中国石化混合所有制经济示范工程山东科鲁尔化学有限公司(简称科鲁尔公司)26万吨/年丙烯腈项目及配套项目二期工程一次开车成功,产出优质产品。从装置投 |
科鲁尔公司 丙烯腈工程开车成功 搜料网资讯:10月底,中国石化混合所有制经济示范工程——山东科鲁尔化学有限公司(简称科鲁尔公司)26万吨/年丙烯腈项目及配套项目二期工程一次开车成功,产出优质产品。从装置投料到产出合格产品仅36小时,创国内同类装置开车最快纪录。 科鲁尔公司是齐鲁石化受集团公司委托与中国万达合资组建的混合所有制企业,把央企在技术、管理和人才上的优势,与民企在区域资源和灵活机制上的优势有机结合,实现优势互补。 该公司位于国家级石油化工产业区之一的东营港经济开发区。此次开车投产的项目采用中国石化自主研发的丙烯氨氧化法技术,采用上海石油化工研究院的先进催化剂。主要产品丙烯腈可制造腈纶、丙烯酰胺、ABS树脂、丁腈橡胶、己二腈等,也可用于其他有机合成和医药工业,用途广泛,前景广阔。 该项目一期工程于2014年12月投产,截至2020年底,工业总产值超过90亿元。二期工程于2020年5月开工,参建各方克服疫情、多雨、生产与施工高度交叉等因素影响,仅用15个月全面建成中交,创国产化程度最高、数字化应用最广等丙烯腈产业基地建设新纪录。 二期工程的建成投产,使科鲁尔公司产能扩大一倍,吨产品能耗、物耗等指标有效摊薄,资源利用率进一步提升,创效能力、抗风险能力和市场竞争能力进一步增强,为打造黄河三角洲高质量发展产业集群再添助力。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 投影仪外壳
- 2019-01-25 0
- LEXAN™ ML6411 resin为聚碳酸酯(PC)硅氧烷树脂,是一种高流动性不透明注塑成型(IM)级,具有极低的温度延性特性。该等级提供基于无氯、无溴阻燃系统的UL94V0@1.5mm和5VA@3.0mm阻燃性
- 阅读全文
投影仪外壳
1-LEXAN™ ML6411 resin为聚碳酸酯(PC)硅氧烷树脂,是一种高流动性不透明注塑成型(IM)级
2-熔体体积流动速率(260℃,5 kg) 18.0 cm³/10min
3-弯曲模量(50 mm跨距) 2600 MPa
4-悬臂梁缺口冲击强度(23℃) 60 kJ/m²
5-热变形温度(1.8 MPa,未退火,100 mm跨距) 115 ℃
6-阻燃等级(1.50 mm) V-0
2-熔体体积流动速率(260℃,5 kg) 18.0 cm³/10min
3-弯曲模量(50 mm跨距) 2600 MPa
4-悬臂梁缺口冲击强度(23℃) 60 kJ/m²
5-热变形温度(1.8 MPa,未退火,100 mm跨距) 115 ℃
6-阻燃等级(1.50 mm) V-0
收起