| 牌号简介 About |
|---|
| Lexan ML6411树脂Lexan ML6411聚碳酸酯（PC）硅氧烷树脂，是一种高流动性不透明注塑成型（IM）级，具有极低的温度延性特性。该等级提供基于无氯、无溴阻燃系统的UL94V0@1.5mm和5VA@3.0mm阻燃性。与标准PC相比，LEXAN™ ML6411 resin具有出色的加工特性，有机会缩短IM周期。该产品有多种不透明颜色，是广泛电气应用的理想选择。 LEXAN ML6411 polycarbonate (PC) siloxane resin, is a high flow opaque injection molding (IM) grade with very low temperature ductility characteristics. This grade offers UL94 V0 @ 1.5mm and 5VA @ 3.0mm flame retardancy based on non-chlorine, non-bromine FR systems. LEXAN ML6411 resin offers excellent processing characteristics with opportunity for shorter IM cycle times compared to standard PC. This product is available in a wide range of opaque colors and is an excellent candidate for a wide range of electrical applications. |
产品描述 Product Description
用途：电气/电子应用领域;
颜色：不透明
加工条件：注射成型 Injection Molding
性能特点： 无卤; 防火阻燃等级V-0; 成型周期快; 防火阻燃等级5VB; 机械强度好-延展; 流动性高; 阻燃; 防火阻燃等级5VA; 易加工; Excellent Processability,High liquidity,Ductility,Quick molding cycle,Halogen free,Flame Characteristics,V-0,5VA,5VB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.19 | g/cm³ | ASTM D792 |
|
密度 Density |
1.20 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
260℃，2.16kg 260℃，2.16kg |
7.0 | g/10min | ASTM D1238 |
|
300℃，1.2kg 300℃，1.2kg |
15 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
260℃，5 kg 260℃，5 kg |
18.0 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
% | 内部方法 | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
断裂 fracture |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/50 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
屈服 yield |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
50 mm跨距 50 mm span |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
屈服，50 mm跨度 Yield, 50 mm span |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-30℃ -30℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Total Energy 23℃，Total Energy |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
1.8 MPa，未退火，100 mm跨距 1.8 MPa, unannealed, 100 mm span |
℃ | ISO 75-2/Ae | |
|
0.45 MPa，未退火，6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，100 mm跨距 0.45 MPa, unannealed, 100 mm span |
℃ | ISO 75-2/Be | |
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 9 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
球压测试 Ball pressure test |
|||
|
125℃ 125℃ |
IEC 60695-10-2 | ||
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ASTM E831 | |
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ISO 11359-2 | |
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ASTM E831 | |
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ISO 11359-2 | |
|
相对温度指数 Relative temperature index |
|||
|
电气性能 Electrical performance |
℃ | UL 746 | |
|
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
|||
|
3.2 mm，在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
高电弧燃烧指数（HAI） High Arc Burning Index (HAI) |
UL 746 | ||
|
热丝引燃 Hot wire ignition |
|||
|
HWI HWI |
UL 746 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
2.00 mm 2.00 mm |
UL 94 | ||
|
3.00 mm 3.00 mm |
UL 94 | ||
|
3.00 mm 3.00 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
|||
|
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
|
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
|
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
|
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.0 in/min |
| 3 类型 1, 2.0 in/min |
| 4 0.051 in/min |
| 5 0.079 in/min |
| 6 Yield |
| 7 80*10*3 |
| 8 120*10*4 mm |
| 9 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
NAPCOR报告显示，美国对rPET的需求在2020年随着收集量的下降而增长
2021-11-09 搜料网资讯： 美国、加拿大和墨西哥在疫情出现的第一年期间的PET回收趋势是国家PET容器资源协会（NAPCOR）最新发布的《2020年PET回收报告》的重点。 该协会在北卡罗来纳州夏洛特市发 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |