牌号简介 About |
---|
Cristal™ 401共聚酯是一种高流动性产品,含有脱模剂,便于脱模。它是专为化妆品包装应用而设计的。凭借其无与伦比的颜色和清晰度,以及一个无与伦比的能力,以改进的门美学模具厚的部分,Cristal显然是一个非常适合的高档化妆品包装共聚酯。Cristal的其他突出特点是优良的耐化学性、高光泽和加工改进,例如更快的循环时间和更低的废品率。Cristal由于其较低的加工温度、非常缓慢的结晶速度和流动特性,也非常适合于两种注射成型技术。 Cristal™ 401 copolyester is a high flow product that contains mold release for ease of ejection. It is designed and engineered specifically for cosmetics packaging applications. With its unsurpassed color and clarity and an unmatched ability to mold thick parts with improved gate aesthetics, Cristal™ is clearly a well suited copolyester for premium cosmetics packaging. Other outstanding features of Cristal™ are excellent chemical resistance, high gloss, and improvements in processing such as faster cycle times, and lower scrap rates. Cristal™ is also ideally suited for two-shot molding techniques due to its lower processing temperatures, very slow crystallization rate, and flow characteristics. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.28 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.20 到 0.50 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-40℃ -40℃ |
44 | J/m | |
23℃ 23℃ |
100 | J/m | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-40℃ -40℃ |
无断裂 | ||
23℃ 23℃ |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
塑料袋成“千年危难” 白色净化成绩如何破解?
2016-02-15 据报道,塑料袋对于现代人来说是再平常不过了,也可以说是一种生活的必需品。尤其是节假日期间,塑料袋的使用更为集中。虽然我国在2008年6月1号出台了“限塑令”,禁止生产、销售和使用超薄塑料购物袋,实行塑料购物袋有偿使用制度,但这一规定如今似乎逐渐被人们遗忘。不仅集贸市场的超薄塑料购物袋大行其道,商场、超市内大量的免费塑料袋也让限塑令的执行效果大打折扣。 难以降解的塑料袋 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |