| 牌号简介 About |
|---|
| Vydyne® 47H BG0693是一种通用的冲击改性PA66树脂。米色可选，热稳定，提高耐高温性能。Vydyne® 47H BG0693的热稳定包装是为了在预期持续或延长高温暴露的应用中使用时提供热耐久性而制定的。Vydyne® 47H BG0693是公认的所有加工和性能优势固有的PA66与提高冲击强度。该树脂具有高熔点、良好的表面润滑性、耐磨性和对许多化学品、机器和汽车油、溶剂和汽油的抵抗力等工程性能的良好平衡组合。Vydyne® 47H BG0693的设计是为了满足许多汽车技术规格中提出的关键低温冲击要求。 Vydyne 47H BG0693 is a general-purpose, impact-modified PA66 resin. Available in beige, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne 47H BG0693 was formulated to provide thermal endurance when used in applications in which continuous or extended high-temperature exposure is anticipated. Vydyne 47H BG0693 is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. Vydyne 47H BG0693 is designed to meet the critical low-temperature impact requirements called out in many automotive specifications. |
产品描述 Product Description
用途：汽车领域的应用;电气/电子应用领域;工业应用;连接器;消费品应用领域;齿轮;紧固件;
颜色：米黄色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 热稳定性好; 耐磨; 耐油; 耐汽油; 耐化学性; 耐低温冲击; 耐低温韧性; 冲击性能好; 韧性好; 易加工; Excellent Processability,Good flexibility,High impact resistance,Good wear resistance,Grease resistance,Solvent resistance,Low temperature toughness,low-temperature impact resistance,Gasoline resistance,Heat Stabilized,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.10 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
ISO 294-4 | ||
|
TD：23℃，2.0 mm TD：23℃，2.0 mm |
1.6 | % | ISO 294-4 |
|
MD：23℃，2.0 mm MD：23℃，2.0 mm |
1.8 | % | ISO 294-4 |
|
吸水率 Water absorption rate |
|||
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
2.3 | % | ISO 62 |
|
23℃，24hr 23℃，24hr |
1.2 | % | ISO 62 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
23℃ 23℃ |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
|
屈服，23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
|
-40℃ -40℃ |
kJ/m² | ISO 179 | |
|
-30℃ -30℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
|
-30℃ -30℃ |
ISO 179 | ||
|
23℃ 23℃ |
ISO 179 | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
|
-40℃ -40℃ |
kJ/m² | ISO 180 | |
|
-30℃ -30℃ |
kJ/m² | ISO 180 | |
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：23~55℃，2 mm TD：23~55℃，2 mm |
1/℃ | ISO 11359-2 | |
|
MD：23~55℃，2 mm MD：23~55℃，2 mm |
1/℃ | ISO 11359-2 | |
|
相对温度指数 Relative temperature index |
|||
|
电气性能 Electrical performance |
UL 746 | ||
|
0.75 mm 0.75 mm |
℃ | UL 746 | |
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
强度机械性能 Strength mechanical performance |
UL 746 | ||
|
0.75 mm 0.75 mm |
℃ | UL 746 | |
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
UL 746 | ||
|
0.75 mm 0.75 mm |
℃ | UL 746 | |
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
|||
|
0.75 mm 0.75 mm |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
|||
|
1 mm 1 mm |
kV/mm | IEC 60243 | |
|
耐电弧性 Arc resistance |
ASTM D495 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
|||
|
3.00 mm 3.00 mm |
V | IEC 60112 | |
|
高电弧燃烧指数（HAI） High Arc Burning Index (HAI) |
UL 746 | ||
|
0.75 mm 0.75 mm |
UL 746 | ||
|
1.5 mm 1.5 mm |
UL 746 | ||
|
3.0 mm 3.0 mm |
UL 746 | ||
|
高电压电弧起痕速率 High voltage arc marking rate |
|||
|
HVTR HVTR |
UL 746 | ||
|
热丝引燃 Hot wire ignition |
|||
|
HWI HWI |
UL 746 | ||
|
0.75 mm 0.75 mm |
UL 746 | ||
|
1.5 mm 1.5 mm |
UL 746 | ||
|
3.0 mm 3.0 mm |
UL 746 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
0.75 mm 0.75 mm |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
3.00 mm 3.00 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
|
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
|
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
|
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
|
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
|
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
|
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
汽车材料 Automotive materials |
|||
|
thickness d = 1 mm thickness d = 1 mm |
FMVSS 302 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
CFRP极受高端用户欢迎但如何降低成本仍需挑战
2021-04-09 搜料网资讯： CFRP是一种碳纤维轻量化材料，能显著减轻产品的重量，因此它是提高能源利用效率理想材料之一。由于CFRP材料具备的优良属性，包括高刚性和高强度属性，促进该材料市 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |