牌号简介 About |
---|
STYRON X-TECH™ 2175是一种环境应力抗裂(ESCR)HIPS树脂,特别是为热成型和挤压而开发,特别是为制冷行业生产冰箱和冰箱的内衬。基于获得专利的Trinseo技术,该树脂通过其独特的ESCR、刚性和熔融强度组合,允许潜在5%的内衬管热成型平均板材挤压厚度的下调。主要特点允许将ESCR向下测量为食品和碳氢化合物,便于在挤压和热成型过程中加工。良好的热成型性能提高了刚性应用大型设备/制冷内衬一般挤压/热成型应用要求ESCR符合欧洲法规(EC)10/2011 FDA,21《美国联邦法规汇编》第177.1640章,详细内容请参考法规。 STYRON X-TECH™ 2175 is an environmental stress crack resistant (ESCR) HIPS resin especially developed for thermoforming and extrusion, especially for the refrigeration industry, the production of inner liners for fridges and freezers. Based on patented Trinseo technology, this resin allows potentially 5 % down gauging of the average sheet extrusion thickness for thermoforming of the inner liners, through its unique combination of ESCR, rigidity and melt strength. Main Characteristics Allows for downgauging ESCR to food stuff and hydrocarbons Ease of processing in extrusion and thermoforming Excellent thermoforming behaviour Increased rigidity Applications Large appliances / refrigeration liners General extrusion/thermoforming applications requiring ESCR Complies with Europe Regulation (EC) 10/2011 FDA, 21 CFR 177.1640 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ASTM D792 |
表观密度 Apparent density |
0.60 | g/cm³ | ASTM D1895 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
2.6 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 3 |
1700 | MPa | ASTM D638 |
-- -- |
1700 | MPa | ISO 527-2/5 |
拉伸强度 tensile strength |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
-- -- 4 |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 4 |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A120 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 6 |
|||
1.50 mm 1.50 mm |
UL 94 |
备注 |
---|
3、5.0 mm/min |
4、方法 I (三点负荷), 1.3 mm/min |
5、标准 B (120°C/h), 压 力1 (10N) |
6、这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
李克强主持召开国常会 部署进一步抓好春季农业生产的措施
2022-04-23 新华社北京4月20日电 国务院总理李克强4月20日主持召开国务院常务会议,部署进一步抓好春季农业生产的措施,确保粮食丰收和重要农产品稳定供应;确定能源保供增供举措,提升能源 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |