K-Resin® SBC KR53是一种丁苯共聚物(SBC)材料,。 该产品在北美洲有供货,。 K-Resin® SBC KR53的主要特性有: 高光泽度 良好的密封性能 良好的韧性 透明度 典型应用领域包括: 包装 标签 电影 食品接触应用 医疗/保健 K-Resin® KR53 makes a clear, stiff, very tough, high gloss film suitable for applications such as candy twist wrap, shrink sleeves and overwrap. FEATURES Excellent Clarity High Surface Gloss Good Toughness Good Heat Sealability APPLICATIONS Medical Packaging Produce Packaging Twist Wrap Lidstock and Labeling Film |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.02 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
10 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
割线模量 Secant modulus |
|||
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
590 | MPa | ASTM D882 |
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
750 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
TD,25 µm,吹塑薄膜 TD, 25 µ m, blow molded film |
g | ASTM D1922 | |
MD,25 µm,吹塑薄膜 MD, 25 µ m, blow molded film |
g | ASTM D1922 | |
氧传输速率 Oxygen transfer rate |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
cm³·mm/m²/atm/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g·mm/m²/atm/24 hr | ASTM F1249 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
0.0254 mm,吹塑薄膜 0.0254 mm, blow molded film |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
25.4 µm,吹塑薄膜 25.4 µ m, blow molded film |
ASTM D523 | ||
雾度 Haze |
|||
25.4 µm,吹塑薄膜 25.4 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
乘用车销量延续七个月负增长 同比大跌17.7%创记载
2019-02-19 导 1月乘用车销量受经济放缓和假期因素影响持续放缓,降幅较上月进一步扩大,但新能源车继续表现出色。 1月 汽车销量放缓的原因可能是经济放缓叠加春节效应。中汽协助理秘书长 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |