| 牌号简介 About |
|---|
| 特点：中等流量，最小模具。用途：按钮及压入式紧固件、水暖五金、齿轮、轴承、电子零件、汽车零件、家用电器等注塑件。又称台湾面 Characteristics: medium flow, minimal mould. Application: Buttons and press-in fasteners, Plumbing and hardware, Gears, Bearing, Electronic Parts, Automotive parts, Household appliances, and Other injection parts. Also known as FORMOSACON |
产品描述 Product Description
用途：纽扣;齿轮;
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 流动性中等; Moderate liquidity,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.41 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
13 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.0 mm MD：3.0 mm |
1.8 到 2.2 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
平衡，23℃，69% RH Equilibrium, 23 ℃, 69% RH |
0.22 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
59 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
熔融温度 Melting temperature |
℃ | DSC | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ASTM D696 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity 3 |
ohms | ASTM D257 | |
|
体积电阻率 Volume resistivity 3 |
|||
|
23℃ 23℃ 3 |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
|||
|
2 mm 2 mm |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
IEC 60250 | ||
|
50 Hz 50 Hz |
IEC 60250 | ||
|
1 kHz 1 kHz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ASTM D785 | ||
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
ASTM D695 | ||
|
1% 应变 1% strain |
MPa | ASTM D695 | |
|
10% 应变 10% strain |
MPa | ASTM D695 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 50%RH |
|
【新闻资讯】查看全部 
我国钛白粉企业循环经济展开力度加大
2016-01-26 近期，国家层面上稳增长政策的各项政策频频出台，国家发展改革委主任徐绍史指出，现在正在采取各种措施是“三大需求”，即投资、消费、净出口。 我国钛白粉企业循环经济发展力度加大 < |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付