CALIBRE™ 5201-8 聚碳酸酯树脂中添加了20%的玻璃纤维增强材料,并加入了脱模剂以优化加工流程。这种树脂具有高模量和优异的尺寸稳定性。CALIBRE 5201-8树脂一般是用于电子产品市场。CALIBRE 5201-8 树脂已经根据ISO 10993 (医疗器械生物学评价)经过了生物相容性测试,适合用于获准的医疗应用领域。 主要特性: 玻璃纤维增强 阻燃 ISO 10993 应用领域: 配电箱 照明元器件 电接头 医疗应用领域 CALIBRE™ 5201-8 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALIBRE 5201-8 resin is typically used in electrical market applications. CALIBRE 5201-8 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Main Characteristics: Glass reinforced Ignition resistant Tested under ISO 10993 Applications: Electrical boxes Lighting components Electrical connectors Medical applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.36 | g/cm³ | ASTM D792 |
密度 Density |
1.36 | g/cm³ | ISO 1183/B |
密度 Density |
1.33 | g/cm³ | ISO 1183-3 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
8.0 | g/10min | ISO 1133 |
300℃,1.20kg 300℃,1.20kg |
8.0 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
|||
MD MD |
% | ASTM D955 | |
MD MD |
% | ISO 294-4 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA 3 | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eA 3 | |
简支梁冲击强度 Charpy impact strength |
|||
23℃ 23℃ |
ISO 179/1eU 3 | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU 3 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 7 |
|||
23℃,Total Energy 23℃,Total Energy 7 |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa 1.8 MPa |
℃ | ISO 75-2 3 | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-2 3 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 8 | |
B50 B50 |
℃ | ISO 306 | |
B50 B50 |
℃ | ISO 306 3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 3 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 9 |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
阻燃等级 Flame retardant level |
|||
3.20 mm 3.20 mm |
ISO 1210 3 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 4 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 3 | |
拉伸强度 tensile strength 4 |
|||
断裂 fracture 4 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield |
MPa | ISO 527-2 3 | |
屈服 yield 4 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 3 | |
屈服 yield |
% | ISO 527-2/50 | |
Nominal strain at break Nominal strain at break |
% | ISO 527-2 3 | |
弯曲模量 Bending modulus 5 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 5 |
MPa | ASTM D790 | |
弯曲强度 bending strength 6 |
MPa | ISO 178 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
ISO 1210 3 |
备注 |
---|
1 Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test. |
2 一般属性:这些不能被视为规格。 |
3 ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
4 2.0 in/min |
5 方法 I (三点负荷), 0.079 in/min |
6 0.079 in/min |
7 11.1 ft/sec |
8 速率 A (50°C/h), 载荷2 (50N) |
9 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
5年关改搬转439家化企!湖北壮士断腕破解“化工围江”
2022-05-31 5月29日,中共湖北省委喜迎党代会 荆楚谱新篇系列新闻发布会第八场在武汉举行,主题为做强战略性新兴产业新引擎,打造全国先进制造业高地。 据湖北省经信厅厅长刘海军介绍,五 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |