PC，CALIBRE™ 5201-8对比PC，Iupilon® GS2020MN1物性表,价格行情_搜料

牌号信息	CALIBRE™ 5201-8 物性表 PC & 美国盛禧奥指导价格：暂无塑料库存：缺货	Iupilon® GS2020MN1 物性表 PC & 日本三菱指导价格：暂无塑料库存：缺货
牌号简介	CALIBRE™ 5201-8 聚碳酸酯树脂中添加了20%的玻璃纤维增强材料，并加入了脱模剂以优化加工流程。这种树脂具有高模量和优异的尺寸稳定性。CALIBRE 5201-8树脂一般是用于电子产品市场。CALIBRE 5201-8 树脂已经根据ISO 10993 (医疗器械生物学评价)经过了生物相容性测试，适合用于获准的医疗应用领域。主要特性：玻璃纤维增强阻燃 ISO 10993 应用领域：配电箱照明元器件电接头医疗应用领域 CALIBRE™ 5201-8 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALIBRE 5201-8 resin is typically used in electrical market applications. CALIBRE 5201-8 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Main Characteristics: Glass reinforced Ignition resistant Tested under ISO 10993 Applications: Electrical boxes Lighting components Electrical connectors Medical applications	Iupilon® GS2020MN1是一种聚碳酸酯（PC）材料,含有的填充物为20% 玻璃纤维增强材料。该产品在北美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 Iupilon® GS2020MN1的主要特性有: 阻燃/额定火焰 Flame Retardant Iupilon® GS2020MN1 is a Polycarbonate (PC) material filled with 20% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® GS2020MN1 are: Flame Rated Flame Retardant

产品描述
厂家：	美国盛禧奥 Trinseo	日本三菱 Mitsubishi
类别：	PC Polycarbonate	PC Polycarbonate
填料：	玻璃纤维 20	玻璃纤维 20
用途：	照明应用,医疗/护理用品,电气/电子应用领域
性能特点：	易加工,尺寸稳定性好,生物兼容性,阻燃,防火阻燃等级V-2,防火阻燃等级V-0 Excellent Processability,Good Dimensional Stability,Biocompatible,Flame Characteristics,V-2,V-0	阻燃,防火阻燃等级V-0 Flame Characteristics,V-0
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL CALIBRE™ 5201-8 Iupilon® GS2020MN1 单位
UNIT 测试方法
TEST METHOD

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ ISO 1183-3

密度
Density g/cm³ ISO 1183/B

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ISO 1133

冲击性能
IMPACT CALIBRE™ 5201-8 Iupilon® GS2020MN1 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁冲击强度(-30℃)
Charpy impact strength kJ/m² ISO 179/1eU 3

简支梁冲击强度(23℃)
Charpy impact strength ISO 179/1eU 3

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA 3

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA 3

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL CALIBRE™ 5201-8 Iupilon® GS2020MN1 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa)
Hot deformation temperature ℃ ISO 75-2 3

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(0.45 MPa，退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa)
Hot deformation temperature ℃ ISO 75-2 3

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/A

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2 3

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306 3

阻燃性能
FLAMMABILITY CALIBRE™ 5201-8 Iupilon® GS2020MN1 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.75 mm)
Flame retardant level UL 94

阻燃等级(1.60 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

阻燃等级(3.20 mm)
Flame retardant level ISO 1210 3

机械性能
MECHANICAL CALIBRE™ 5201-8 Iupilon® GS2020MN1 单位
UNIT 测试方法
TEST METHOD

Nominal strain at break
Nominal strain at break % ISO 527-2 3

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2 3

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2 3

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2 3

拉伸模量
Tensile modulus MPa ISO 527-2/50

洛氏硬度(R 级)
Rockwell hardness ASTM D785

电气性能
ELECTRICAL CALIBRE™ 5201-8 Iupilon® GS2020MN1 单位
UNIT 测试方法
TEST METHOD

相比漏电起痕指数
Compared to the leakage tracing index UL 746

加工方式

注射 CALIBRE™ 5201-8 Iupilon® GS2020MN1 单位测试方法

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

螺杆转速 rpm

备注

1 Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test.

2 一般属性：这些不能被视为规格。

3 ??????,?? ISO 10350 ??? 23°C/50%r.h. ???

4 2.0 in/min

5 方法 I (三点负荷), 0.079 in/min

6 0.079 in/min

7 11.1 ft/sec

8 速率 A (50°C/h), 载荷2 (50N)

9 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
阻燃性能
机械性能
电气性能
加工方式
注射
备注