牌号简介 About |
---|
用途:用于购物和杂货袋,穿孔辊,垃圾袋和工业内衬。特点:双峰吹塑薄膜级,具有较高的拉伸和冲击强度,良好的刚度和阻隔性能,分子量分布广,易于加工。在重载条件下性能良好。 Applications: For shopping and grocery bags, perforated rolls, trash bags, and industrial liners. Characteristics: Bimodal blown film grade having high tensile and impact strength, good stiffness and barrier properties with a wide molecular weight distribution for easy processing. Performs well under heavy load conditions. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.951 | g/cm³ | ASTM D792-A |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.050 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
9.3 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 - 1% 正割,MD Secant modulus -1% secant, MD |
ASTM D882 | ||
-- -- 2 |
990 | MPa | ASTM D882 |
-- -- 3 |
930 | MPa | ASTM D882 |
割线模量 - 1% 正割,TD Secant modulus -1% secant, TD |
ASTM D882 | ||
-- -- 2 |
MPa | ASTM D882 | |
-- -- 3 |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ASTM D882 | |
MD,屈服 MD, yield |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
TD,屈服 TD, yield |
MPa | ASTM D882 | |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂 MD, fracture 2 |
MPa | ASTM D882 | |
MD,断裂 MD, fracture 3 |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
TD,断裂 TD, fracture 2 |
MPa | ASTM D882 | |
TD,断裂 TD, fracture 3 |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture 2 |
% | ASTM D882 | |
MD,断裂 MD, fracture 3 |
% | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
TD,断裂 TD, fracture 2 |
% | ASTM D882 | |
TD,断裂 TD, fracture 3 |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
ASTM D1709 | ||
-- -- 2 |
g | ASTM D1709 | |
-- -- 3 |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 - MD Elmandorf Tear Strength - MD |
ASTM D1922 | ||
-- -- 2 |
g | ASTM D1922 | |
-- -- 3 |
g | ASTM D1922 | |
撕裂强度 tear strength |
ASTM D1922 | ||
TD TD 2 |
g | ASTM D1922 | |
TD TD 3 |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 With stabilizer |
3 without stabilizer |
4 With Stabilizer |
5 Without stabilizer |
6 速率 A (50°C/h), 压 力1 (10N) |
【新闻资讯】查看全部
石化代表供应侧改革观:辞别散乱差才好赚钱
2016-03-11 “需求下滑、销售额下滑、利润下滑”,让尚舜化工董事长徐承秋代表满脸愁云,“我们行业100多家企业,五六成快撑不住了。” 同样为前景发愁的,还有东明石化董事长李湘平代表,“炼油行业的产能过剩比钢铁行业还严重。钢铁企业开工率约为75%,炼油企业只有68%。” 眼下,在石化行业,无论是徐承秋,还是李湘平,都在苦苦寻求供给侧的“加减法”。 根据中国石化工业联合会发布的报告,中国石化行业2015年全年增加值同比增8.7%,主营业务收入下降5.5%,利润 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |