牌号简介 About |
---|
Ultramid® A3EG7是一种35%玻璃纤维增强注塑成型PA66级机械部件和外壳的高刚度和尺寸稳定性。典型应用包括灯插座外壳、冷却风扇、铝窗框的绝缘轮廓、汽车冷却系统的水容器以及电绝缘部件。 Ultramid A3EG7 is a 35% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. Applications Typical applications include lamp socket housings, cooling fans, insulating profile for aluminium window frames, water containers for automotive cooling systems, as well as electrically insulating parts. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.410 | g/cm³ | ISO 1183 |
粘度 viscosity |
145 | g/cm³ | ISO 307, 1157, 1628 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH,2.00 mm Equilibrium, 23 ℃, 50% RH, 2.00 mm |
1.40-1.80 | % | ISO 62 |
饱和 saturated |
4.7-5.3 | ISO 62 | |
卤素含量 Halide Content |
|||
CI,Br,1 CI,Br,1 |
< 100 | mg/kg | 舍格尼IC |
融化温度 Melting temperature |
°C | ISO 11357-1/-3 | |
熔体体积流动速率 Melt Volume Rate |
|||
275℃,5 kg 275℃,5 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
|||
MD MD |
% | ||
TD TD |
% | ISO 294-4 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
kJ/m² | ISO 180/1A | |
23℃ 23℃ |
KJ/m² | ISO 180/1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 |
|||
纵向:23-80℃ Vertical: 23-80 ℃ |
E-6/k | ISO 11359-1/-2 | |
横向:23~80℃ Horizontal: 23~80 ℃ |
E-6/k | ISO 11359-1/-2 | |
熔融温度 Melting temperature |
℃ | ||
热变形温度 Hot deformation temperature |
|||
0.45 MPa 0.45 MPa |
℃ | ISO 75-1/2 | |
热变形温度 Hot deformation temperature |
|||
1.8 MPa 1.8 MPa |
℃ | ISO 75-1/2 | |
比热容 Specific heat capacity |
J/(kg*K) | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.6mm 1.6mm |
IEC 60695-11-10 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲强度 bending strength |
MPa | ISO 178 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
% | ISO 527-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相对电容率 Relative permittivity |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1MHz 1MHz |
E-4 | IEC 60250 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
科思创与伟翔签署合作意向书,共建废弃电器电子领域塑料循环再生价
2021-11-11 搜料网资讯: ●提升废弃电器电子产品中塑料的回收再利用价值 ●为聚碳酸酯等工程塑料建立循环供应链及商业模式 ●助力双碳目标,推动中国经济高质量可持续发展 在第四届中国国 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |