NITRIFLEX N-8是一种丁腈橡胶 (NBR)产品,。 它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 主要特性为:炭黑。 Texin 985 resin is an aromatic polyether-based thermoplastic polyurethane with a Shore hardness of approximately 85A. It can be processed by injection molding, extrusion, or blow molding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.12 | g/cm³ | ASTM D792 |
密度 Density |
1.12 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 2577 | ||
TD:2.54 mm TD:2.54 mm |
0.80 | % | ASTM D955 |
MD:2.54 mm MD:2.54 mm |
0.80 | % | ASTM D955 |
TD:2.54 mm TD:2.54 mm |
0.80 | % | ISO 2577 |
MD:2.54 mm MD:2.54 mm |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
邵氏 A Shaw's A |
ISO 868 | ||
弯曲模量 Bending modulus |
ASTM D790 | ||
-30℃ -30℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
ISO 178 | ||
-30℃ -30℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ISO 4649 | |
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ASTM D1044 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D412 | |
屈服 yield |
MPa | ISO 37 | |
300% 应变 300% strain |
MPa | ISO 37 | |
300% 应变 300% strain |
MPa | ASTM D412 | |
100% 应变 100% strain |
MPa | ISO 37 | |
100% 应变 100% strain |
MPa | ASTM D412 | |
50% 应变 50% strain |
MPa | ISO 37 | |
50% 应变 50% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
断裂 fracture |
% | ISO 37 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
撕裂强度 tear strength |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
ASTM D395B | ||
23℃,22 hr 23℃,22 hr 3 |
% | ASTM D395B | |
23℃,22 hr 23℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr 3 |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
压缩形变 Compression deformation |
ISO 815 | ||
23℃,22 hr 23℃,22 hr 3 |
% | ISO 815 | |
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr 3 |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
脆化温度 Embrittlement temperature |
℃ | ISO 974 | |
玻璃化转变温度 Glass transition temperature |
℃ | DMA | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/50 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ASTM D573 | ||
100℃,70 hr 100℃,70 hr |
% | ASTM D573 | |
100% Strain,100℃,70 hr 100% Strain,100℃,70 hr |
% | ASTM D573 | |
300% Strain,100℃,70 hr 300% Strain,100℃,70 hr |
% | ASTM D573 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
100% Strain,100℃,168 hr 100% Strain,100℃,168 hr |
% | ASTM D573 | |
300% Strain,100℃,168 hr 300% Strain,100℃,168 hr |
% | ASTM D573 | |
100℃,336 hr 100℃,336 hr |
% | ASTM D573 | |
100% Strain,100℃,336 hr 100% Strain,100℃,336 hr |
% | ASTM D573 | |
300% Strain,100℃,336 hr 300% Strain,100℃,336 hr |
% | ASTM D573 | |
100℃,504 hr 100℃,504 hr |
% | ASTM D573 | |
100% Strain,100℃,504 hr 100% Strain,100℃,504 hr |
% | ASTM D573 | |
300% Strain,100℃,504 hr 300% Strain,100℃,504 hr |
% | ASTM D573 | |
125℃,70 hr 125℃,70 hr |
% | ASTM D573 | |
100% Strain,125℃,70 hr 100% Strain,125℃,70 hr |
% | ASTM D573 | |
300% Strain,125℃,70 hr 300% Strain,125℃,70 hr |
% | ASTM D573 | |
125℃,168 hr 125℃,168 hr |
% | ASTM D573 | |
100% Strain,125℃,168 hr 100% Strain,125℃,168 hr |
% | ASTM D573 | |
300% Strain,125℃,168 hr 300% Strain,125℃,168 hr |
% | ASTM D573 | |
125℃,336 hr 125℃,336 hr |
% | ASTM D573 | |
100% Strain,125℃,336 hr 100% Strain,125℃,336 hr |
% | ASTM D573 | |
300% Strain,125℃,336 hr 300% Strain,125℃,336 hr |
% | ASTM D573 | |
125℃,504 hr 125℃,504 hr |
% | ASTM D573 | |
100% Strain,125℃,504 hr 100% Strain,125℃,504 hr |
% | ASTM D573 | |
300% Strain,125℃,504 hr 300% Strain,125℃,504 hr |
% | ASTM D573 | |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ISO 216 | ||
100℃,70 hr 100℃,70 hr |
% | ISO 216 | |
100% Strain 100℃,70 hr 100% Strain 100℃,70 hr |
% | ISO 216 | |
300% Strain 100℃,70 hr 300% Strain 100℃,70 hr |
% | ISO 216 | |
100℃,168 hr 100℃,168 hr |
% | ISO 216 | |
100% Strain 100℃,168 hr 100% Strain 100℃,168 hr |
% | ISO 216 | |
300% Strain 100℃,168 hr 300% Strain 100℃,168 hr |
% | ISO 216 | |
100℃,336 hr 100℃,336 hr |
% | ISO 216 | |
100% Strain 100℃,336 hr 100% Strain 100℃,336 hr |
% | ISO 216 | |
300% Strain 100℃,336 hr 300% Strain 100℃,336 hr |
% | ISO 216 | |
100℃,504 hr 100℃,504 hr |
% | ISO 216 | |
100% Strain 100℃,504 hr 100% Strain 100℃,504 hr |
% | ISO 216 | |
300% Strain 100℃,504 hr 300% Strain 100℃,504 hr |
% | ISO 216 | |
125℃,70 hr 125℃,70 hr |
% | ISO 216 | |
100% Strain 125℃,70 hr 100% Strain 125℃,70 hr |
% | ISO 216 | |
300% Strain 125℃,70 hr 300% Strain 125℃,70 hr |
% | ISO 216 | |
125℃,168 hr 125℃,168 hr |
% | ISO 216 | |
100% 应变 125℃,168 hr 100% strain 125 ℃, 168 hr |
% | ISO 216 | |
300% Strain 125℃,168 hr 300% Strain 125℃,168 hr |
% | ISO 216 | |
125℃,336 hr 125℃,336 hr |
% | ISO 216 | |
100% Strain 125℃,336 hr 100% Strain 125℃,336 hr |
% | ISO 216 | |
300% Strain 125℃,336 hr 300% Strain 125℃,336 hr |
% | ISO 216 | |
125℃,504 hr 125℃,504 hr |
% | ISO 216 | |
100% Strain 125℃,504 hr 100% Strain 125℃,504 hr |
% | ISO 216 | |
300% Strain 125℃,504 hr 300% Strain 125℃,504 hr |
% | ISO 216 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
ASTM D573 | ||
100℃,70 hr 100℃,70 hr |
% | ASTM D573 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
100℃,336 hr 100℃,336 hr |
% | ASTM D573 | |
100℃,504 hr 100℃,504 hr |
% | ASTM D573 | |
125℃,70 hr 125℃,70 hr |
% | ASTM D573 | |
125℃,168 hr 125℃,168 hr |
% | ASTM D573 | |
125℃,336 hr 125℃,336 hr |
% | ASTM D573 | |
125℃,504 hr 125℃,504 hr |
% | ASTM D573 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air |
ISO 216 | ||
100℃,70 hr 100℃,70 hr |
% | ISO 216 | |
100℃,168 hr 100℃,168 hr |
% | ISO 216 | |
100℃,336 hr 100℃,336 hr |
% | ISO 216 | |
100℃,504 hr 100℃,504 hr |
% | ISO 216 | |
125℃,70 hr 125℃,70 hr |
% | ISO 216 | |
125℃,168 hr 125℃,168 hr |
% | ISO 216 | |
125℃,336 hr 125℃,336 hr |
% | ISO 216 | |
125℃,504 hr 125℃,504 hr |
% | ISO 216 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 | ||
邵氏 D,100℃,70 hr Shore D, 100 ℃, 70 hr |
ASTM D573 | ||
邵氏 D,100℃,168 hr Shore D, 100 ℃, 168 hr |
ASTM D573 | ||
邵氏 D,100℃,336 hr Shore D, 100 ℃, 336 hr |
ASTM D573 | ||
邵氏 D,100℃,504 hr Shore D, 100 ℃, 504 hr |
ASTM D573 | ||
邵氏 D,125℃,70 hr Shore D, 125 ℃, 70 hr |
ASTM D573 | ||
支撐 D,125℃,168 hr Support D, 125 ℃, 168 hr |
ASTM D573 | ||
邵氏 D,125℃,336 hr Shaw's D, 125 ℃, 336 hr |
ASTM D573 | ||
邵氏 D,125℃,504 hr Shaw's D, 125 ℃, 504 hr |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 216 | ||
邵氏 D,100℃,70 hr Shore D, 100 ℃, 70 hr |
ISO 216 | ||
邵氏 D,100℃,168 hr Shore D, 100 ℃, 168 hr |
ISO 216 | ||
邵氏 D,100℃,336 hr Shore D, 100 ℃, 336 hr |
ISO 216 | ||
邵氏 D,100℃,504 hr Shore D, 100 ℃, 504 hr |
ISO 216 | ||
邵氏 D,125℃,70 hr Shore D, 125 ℃, 70 hr |
ISO 216 | ||
支撐 D,125℃,168 hr Support D, 125 ℃, 168 hr |
ISO 216 | ||
邵氏 D,125℃,336 hr Shaw's D, 125 ℃, 336 hr |
ISO 216 | ||
邵氏 D,125℃,504 hr Shaw's D, 125 ℃, 504 hr |
ISO 216 | ||
拉伸强度的变化率 The rate of change in tensile strength |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
100% Strain,23℃,70 hr,in Reference Fuel C 100% Strain,23℃,70 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,70 hr,in Reference Fuel C 300% Strain,23℃,70 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
100% Strain,23℃,168 hr,in Reference Fuel C 100% Strain,23℃,168 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,168 hr,in Reference Fuel C 300% Strain,23℃,168 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
100% Strain,23℃,336 hr,in Reference Fuel C 100% Strain,23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,336 hr,in Reference Fuel C 300% Strain,23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100% Strain,23℃,504 hr,in Reference Fuel C 100% Strain,23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,504 hr,in Reference Fuel C 300% Strain,23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100% Strain,100℃,70 hr,in ASTM #1 Oil 100% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,70 hr,in ASTM #1 Oil 300% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100% Strain,100℃,70 hr,in ASTM #3 Oil 100% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,70 hr,in ASTM #3 Oil 300% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,168 hr,in ASTM #1 Oil 100% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,168 hr,in ASTM #1 Oil 300% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,168 hr,in ASTM #3 Oil 100% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,168 hr,in ASTM #3 Oil 300% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,336 hr,in ASTM #1 Oil 100% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,336 hr,in ASTM #1 Oil 300% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,336 hr,in ASTM #3 Oil 100% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,336 hr,in ASTM #3 Oil 300% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,504 hr,in ASTM #1 Oil 100% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,504 hr,in ASTM #1 Oil 300% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,504 hr,in ASTM #3 Oil 100% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,504 hr,in ASTM #3 Oil 300% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
拉伸强度的变化率 The rate of change in tensile strength |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
100% Strain,23℃,70 hr,in Reference Fuel C 100% Strain,23℃,70 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,70 hr,in Reference Fuel C 300% Strain,23℃,70 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
100% Strain,23℃,168 hr,in Reference Fuel C 100% Strain,23℃,168 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,168 hr,in Reference Fuel C 300% Strain,23℃,168 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
100% Strain,23℃,336 hr,in Reference Fuel C 100% Strain,23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,336 hr,in Reference Fuel C 300% Strain,23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100% Strain,23℃,504 hr,in Reference Fuel C 100% Strain,23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,504 hr,in Reference Fuel C 300% Strain,23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100% Strain,100℃,70 hr,in ASTM #1 Oil 100% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,70 hr,in ASTM #1 Oil 300% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100% Strain,100℃,70 hr,in ASTM #3 Oil 100% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,70 hr,in ASTM #3 Oil 300% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,168 hr,in ASTM #1 Oil 100% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,168 hr,in ASTM #1 Oil 300% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,168 hr,in ASTM #3 Oil 100% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,168 hr,in ASTM #3 Oil 300% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,336 hr,in ASTM #1 Oil 100% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,336 hr,in ASTM #1 Oil 300% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,336 hr,in ASTM #3 Oil 100% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,336 hr,in ASTM #3 Oil 300% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,504 hr,in ASTM #1 Oil 100% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,504 hr,in ASTM #1 Oil 300% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,504 hr,in ASTM #3 Oil 100% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,504 hr,in ASTM #3 Oil 300% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
极限伸长率的变化率 Change rate of ultimate elongation |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
断裂时拉伸应力变化 Changes in tensile stress during fracture |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
邵氏硬度的变化率 The rate of change in Shore hardness 2 |
ASTM D471 | ||
邵氏 D,23℃,70 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,70 hr,在基准燃料C中 Shore D, 23°C, 70 hr, in Reference Fuel C |
ASTM D471 | ||
邵氏 D,23℃,168 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,168 hr,在基准燃料中 Shore D, 23 ℃, 168 hr, in reference fuel |
ASTM D471 | ||
邵氏 D,23℃,336 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,336 hr,在基准燃料C中 Shore D, 23 ℃, 336 hr, in reference fuel C |
ASTM D471 | ||
邵氏 D,23℃,504 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,504 hr,,在基准燃料C中 Shore D, 23 ℃, 504 hr, in reference fuel C |
ASTM D471 | ||
邵氏 D,100℃,70 hr,在ASTM #1油中 Shore D, 100°C, 70 hr, in ASTM #1 Oil |
ASTM D471 | ||
邵氏 D,100℃,70 hr,在ASTM #3油中 Shore D, 100 ℃, 70 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,168 hr,在ASTM #1油中 Shore D, 100°C, 168 hr, in ASTM #1 Oil |
ASTM D471 | ||
邵氏 D,100℃,168 hr,在ASTM #3油中 Shore D, 100 ℃, 168 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,336 hr,在ASTM #1油中 Shore D, 100 ℃, 336 hr, in ASTM # 1 oil |
ASTM D471 | ||
邵氏 D,100℃,336 hr,在ASTM #3油中 Shore D, 100 ℃, 336 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,504 hr,在ASTM #1油中 Shore D, 100 ℃, 504 hr, in ASTM # 1 oil |
ASTM D471 | ||
邵氏 D,100℃,504 hr,在ASTM #3油中 Shore D, 100 ℃, 504 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏硬度的变化率 The rate of change in Shore hardness |
ISO 175 | ||
邵氏 D,23℃,70 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,70 hr,在基准燃料C中 Shore D, 23°C, 70 hr, in Reference Fuel C |
ISO 175 | ||
邵氏 D,23℃,168 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,168 hr,在基准燃料中 Shore D, 23 ℃, 168 hr, in reference fuel |
ISO 175 | ||
邵氏 D,23℃,336 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,336 hr,在基准燃料C中 Shore D, 23 ℃, 336 hr, in reference fuel C |
ISO 175 | ||
邵氏 D,23℃,504 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,504 hr,,在基准燃料C中 Shore D, 23 ℃, 504 hr, in reference fuel C |
ISO 175 | ||
邵氏 D,100℃,70 hr,在ASTM #1油中 Shore D, 100°C, 70 hr, in ASTM #1 Oil |
ISO 175 | ||
邵氏 D,100℃,70 hr,在ASTM #3油中 Shore D, 100 ℃, 70 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,168 hr,在ASTM #1油中 Shore D, 100°C, 168 hr, in ASTM #1 Oil |
ISO 175 | ||
邵氏 D,100℃,168 hr,在ASTM #3油中 Shore D, 100 ℃, 168 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,336 hr,在ASTM #1油中 Shore D, 100 ℃, 336 hr, in ASTM # 1 oil |
ISO 175 | ||
邵氏 D,100℃,336 hr,在ASTM #3油中 Shore D, 100 ℃, 336 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,504 hr,在ASTM #1油中 Shore D, 100 ℃, 504 hr, in ASTM # 1 oil |
ISO 175 | ||
邵氏 D,100℃,504 hr,在ASTM #3油中 Shore D, 100 ℃, 504 hr, in ASTM # 3 oil |
ISO 175 | ||
体积变化 Volume change |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A 23℃,70 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A 23℃,168 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A 23℃,336 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A 23℃,504 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
体积变化 Volume change |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A 23℃,70 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A 23℃,168 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A 23℃,336 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A 23℃,504 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩载荷 Compression load |
ASTM D575 | ||
10% 挠曲 10% deflection |
MPa | ASTM D575 | |
15% 挠曲 15% deflection |
MPa | ASTM D575 | |
2% 挠曲 2% deflection |
MPa | ASTM D575 | |
20% 挠曲 20% deflection |
MPa | ASTM D575 | |
25% 挠曲 25% deflection |
MPa | ASTM D575 | |
5% 挠曲 5% deflection |
MPa | ASTM D575 | |
50% 挠曲 50% deflection |
MPa | ASTM D575 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
排名再升17位!恒力再次上榜“世界品牌500强”
2020-12-19 搜料网资讯:12月17日,世界品牌实验室(World Brand Lab)2020年度《世界品牌500强》排行榜揭晓!恒力集团的恒力品牌列总榜第398位,成为国内石化、纺织行业内唯一入围品牌。 品牌是企业 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |