| 牌号简介 About |
|---|
| Daplen™ EF005AE是一种10%矿物填充弹性体改性聚丙烯化合物，用于注塑成型。这种材料在冲击强度和刚度之间具有极好的平衡，具有良好的表面质量，易于加工。 Daplen EF005AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness, gives a good surface quality and is easy to process. Applications Daplen EF005AE has been developed especially for the car industry to be used in automotive exterior parts. Bumpers Exterior trims Spoilers Special Features Suitable for applications, which require low expansion over a broad temperature scale UV stabilised Low in tigerstripes High flowability |
产品描述 Product Description
用途：汽车防撞杆;汽车外部零件;汽车外部装饰;
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 流动性高; 冲击性能好; 耐候抗UV; 表面光泽度好; 易加工; Good Rigidity,Weather resistance is good,Excellent Processability,Good surface appearance,High impact resistance,High liquidity
填料：矿物 10
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.950 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
25 | g/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
Internal Method | ||
|
-- -- 2 |
0.80 | % | 内部方法 |
|
90℃，2 hrs 90℃，2 hrs |
0.15 | % | 内部方法 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
4.0 | kJ/m² | ISO 179/1eA |
|
-20℃ -20℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-20℃ -20℃ |
ISO 179/1eU | ||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
|
-20℃ -20℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
B50 B50 |
℃ | ISO 306 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-30~80℃ MD：-30~80℃ |
1/℃ | 内部方法 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/50 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus 3 |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
MPa | ISO 178 | |
|
球压硬度 Ball hardness |
|||
|
H 132/10 H 132/10 |
MPa | ISO 2039-1 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 disk |
| 3 0.079 in/min |
|
【新闻资讯】查看全部 
生产应急手册:塑料缩水的常见成绩和处理方法下
2018-02-28 8烧焦、气纹 原因分析:一般所谓的烧焦(Burn Mark)包括制品表面因塑胶降解导致的变色及制品的填充末端焦黑的现象。烧焦是滞留型腔内的空气在塑料熔体填充时未能迅速排出(困气)，被压 |
|