LINATHENE® LL120C是一种用于槽铸膜挤出的丁烯线性低密度聚乙烯(LLDPE)。由LINATHENE® LL120C制成的薄膜具有优异的韧性、拉伸强度、延伸率、穿透强度和透明度。推荐LINATHENE® LL120C用于拉伸膜、保鲜膜和农用膜的生产。 LINATHENE LL120C is a butene linear low density polyethylene(LLDPE) developed for slot cast film extrusion. Films made from LINATHENE LL120C have excellent toughness, tensile strength, elongation, puncture strength and transparency. LINATHENE LL120C is recommended for the manufacture of stretch film, cling film and agricultural film. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.919 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
2.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
10.3 | MPa | ASTM D882 |
TD,屈服 TD, yield |
9.32 | MPa | ASTM D882 |
MD,断裂 MD, fracture |
23.5 | MPa | ASTM D882 |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
g | ASTM D1709 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
震惊!人类已消费83亿吨塑料
2017-07-21 发表在最新一期《科学进展》杂志上的一项研究称,20世纪50年代初以来,人类已经生产了83亿吨塑料,其中的大部分成了废弃物,被置于垃圾填埋场或散落在自然环境中,造成的污染问题不容忽视。研究人员呼吁,应对塑料产品使用和废弃物管理问题进行批判性思考,想想在某些情况下使用塑料是否必要。 这项由美国佐治亚大学、加州大学圣巴巴拉分校和海洋教育协会研究人员领导的研究小组,首次对全球所有塑料制品的生产、使用和最终命运进行了分析。研究人员收集了各种工业树脂、纤维和添加剂的生产统计数据,并根据 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |