| 牌号简介 About |
|---|
| LINATHENE® LL120C是一种用于槽铸膜挤出的丁烯线性低密度聚乙烯（LLDPE）。由LINATHENE® LL120C制成的薄膜具有优异的韧性、拉伸强度、延伸率、穿透强度和透明度。推荐LINATHENE® LL120C用于拉伸膜、保鲜膜和农用膜的生产。 LINATHENE LL120C is a butene linear low density polyethylene(LLDPE) developed for slot cast film extrusion. Films made from LINATHENE LL120C have excellent toughness, tensile strength, elongation, puncture strength and transparency. LINATHENE LL120C is recommended for the manufacture of stretch film, cling film and agricultural film. |
产品描述 Product Description
用途：薄膜;农业应用;
加工条件：薄膜挤出 Film extrusion
性能特点： 拉伸性能好; 透光性好; 低密度; 韧性好; 抗穿孔性; Good Clarity,Good flexibility,Good Tensile Strength,Low density,Puncture Resistant
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.919 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
2.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，屈服 MD, yield |
10.3 | MPa | ASTM D882 |
|
TD，屈服 TD, yield |
9.32 | MPa | ASTM D882 |
|
MD，断裂 MD, fracture |
23.5 | MPa | ASTM D882 |
|
TD，断裂 TD, fracture |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
MD，断裂 MD, fracture |
% | ASTM D882 | |
|
TD，断裂 TD, fracture |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact 2 |
g | ASTM D1709 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 F50 |
|
【新闻资讯】查看全部 
常用加强资料与填料速查表
2018-03-09 小编整理了两份常用塑料增强材料、填料及适用树脂以及性能用途的自查表，供大家快速查找，方便高效的选择填料以及增强材料。推荐收藏!!! 表 常用增强材料及填料的性能用途 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付