牌号简介 About |
---|
RP970是一种用于注塑成型的聚丙烯化合物。 RP970 is a polypropylene compound intended for injection moulding. Applications RP970 has been developed especially for the car industry to be used in automotive interior parts. Interior trims Covers Special features Good stiffness and impact balance Very good flow |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.890 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
12 | g/10min | ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
32 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
无断裂 | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
30 | kJ/m² | ISO 180-1A |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ISO 180/1U | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Ae | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.00 mm 1.00 mm |
mm/min | ISO 3795 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 1 |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
【新闻资讯】查看全部
从裁员到放慢重组,巴斯夫逐步展露野心?精简结构、定制服务,加巴
2019-10-23 巴斯夫于7月初宣布下调预期,随即加快脚步裁减人员,预计至2021年底在全球减少6000个工作岗位。近日,巴斯夫欧洲董事会决定自2020年1月1日起将公司执行董事会成员数量从七人减少为 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |