| 牌号简介 About |
|---|
| MAGNUM™ 275 ABS树脂是一种低光泽、低流动性、抗冲击性好的ABS树脂。Magnum ABS树脂是一种热塑性材料，可提供各种聚合物成分所赋予的加工性、抗冲击性和耐热性的极好平衡。Magnum ABS树脂有多种熔体流动速率、冲击强度和耐热性，适用于通过注塑、片材或型材挤压和热成型制造的高光泽和低光泽应用。Magnum ABS树脂为低光泽注塑应用提供了广泛的加工能力和抗冲击性。结合耐热性、拉伸强度和弯曲强度，Magnum ABS树脂可用于各种注塑应用。应用注射成型应用挤压和热成型应用符合：美国FDA 21 CFR 181.32有关完整的详细信息，请参考法规。 MAGNUM™ 275 ABS resin is a low gloss, low flow ABS resin with good impact. MAGNUM ABS resins are thermoplastic materials that provide an excellent balance of processability, impact resistance, and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resins are available in a wide range of melt flow rates, impact strengths, and heat resistances for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion, and thermoforming. MAGNUM ABS resins offer a wide range of processing abilities and impact resistance for low gloss injection molding applications. Combined with heat resistance, tensile and flexural strength, MAGNUM ABS resins are used in a wide variety of injection molding applications. Applications Injection molding applications Extrusion and thermoforming applications Complies with: U.S. FDA 21 CFR 181.32 Consult the regulations for complete details. |
产品描述 Product Description
加工条件：挤出 Extrusion
性能特点： 防火阻燃等级HB; 流动性低; 耐高温; 低光泽; 冲击性能好; 易加工; Excellent Processability,Low liquidity,High impact resistance,High Heat Resistance,Low Gloss,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.04 | g/cm³ | ASTM D792 |
|
密度 Density |
1.05 | g/cm³ | ISO 1183-2 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，3.80kg 230℃，3.80kg |
2.6 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
220℃，10 kg 220℃，10 kg |
9.00 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.40 to 0.70 | % | ASTM D955 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 3 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 2 | |
|
拉伸强度 tensile strength 4 |
|||
|
断裂 fracture 4 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2 2 | |
|
屈服 yield 4 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture 4 |
% | ASTM D638 | |
|
屈服 yield 4 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2 2 | |
|
Nominal strain at break Nominal strain at break |
% | ISO 527-2 2 | |
|
弯曲模量 Bending modulus 5 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 5 |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA 2 | |
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA 2 | |
|
简支梁冲击强度 Charpy impact strength |
|||
|
23℃ 23℃ |
ISO 179/1eU 2 | ||
|
-30℃ -30℃ |
ISO 179/1eU 2 | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 6 |
ASTM D256 | ||
|
-18℃，3.2mm -18℃，3.2mm |
J/m | ASTM D256 | |
|
23℃，3.2mm 23℃，3.2mm |
J/m | ASTM D256 | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
|
-18℃，Peak Energy -18℃，Peak Energy |
J | ASTM D3763 | |
|
-18℃，3.20 mm，Total Energy -18℃，3.20 mm，Total Energy 7 |
J | ASTM D3763 | |
|
23℃，Peak Energy 23℃，Peak Energy |
J | ASTM D3763 | |
|
23℃，3.20 mm，Total Energy 23℃，3.20 mm，Total Energy 7 |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa 1.8 MPa |
℃ | ISO 75-2 2 | |
|
0.45 MPa，未退火，3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
0.45 MPa 0.45 MPa |
℃ | ISO 75-2 2 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
B50 B50 |
℃ | ISO 306 2 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ISO 11359-2 2 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level 8 |
|||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
阻燃等级 Flame retardant level |
|||
|
1.60 mm 1.60 mm |
ISO 1210 2 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 39 in/min |
| 4 类型 1, 2.0 in/min |
| 5 类型 1, 79 in/min |
| 6 10 mil 缺口深度 |
| 7 11.1 ft/sec |
| 8 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
|
【新闻资讯】查看全部
美对华零售用聚乙烯塑料袋发布双反继续征税令
2016-05-10 2016年5月5日，美国商务部发布公告，对中国、印度尼西亚、马来西亚、台湾地区、泰国和越南的零售用聚乙烯塑料袋(Polyethylene Retail Carrier Bags，简称PRCB)发布反倾销继续征税令;同时对越南的涉案产品发布反补贴继续征税令。自本公告发布之日起开始征税，征税期为五年。涉案产品为由厚度为0.00035英寸(0.00889毫米)~0.035英寸(0.889毫米)、长或宽为6英寸(15.24厘米)~40英寸(101.6厘米)的聚乙烯薄膜制成的带手柄非密封袋。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付