| 牌号简介 About |
|---|
| Lexan CFR9712树脂Lexan CFR9712聚碳酸酯（PC）树脂是一种非填充、注射成型级树脂。这种无氯化、无溴阻燃PC具有2.0 mm的UL-94V0额定值和高流动性。Lexan CFR9712提供透明和着色的颜色选择，非常适合各种应用。 LEXAN CFR9712 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 2.0 mm and high flow capability. LEXAN CFR9712 is available in clear transparent and tinted color options that is an excellent candidate for a wide variety of applications. |
产品描述 Product Description
颜色：清晰/透明,可用颜色
加工条件：注射成型 Injection Molding
性能特点： 无卤; 防火阻燃等级V-1; 防火阻燃等级V-0; 防火阻燃等级V-2; 流动性高; 阻燃; High liquidity,Halogen free,Flame Characteristics,V-2,V-1,V-0
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
|||
|
-- -- |
1.19 | g/cm³ | ASTM D792 |
|
-- -- |
1.20 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
30 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
300℃，1.2 kg 300℃，1.2 kg |
29.0 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
内部方法 | ||
|
MD：3.2 mm MD：3.2 mm |
0.55 到 0.75 | % | 内部方法 |
|
TD：3.2 mm TD：3.2 mm |
% | 内部方法 | |
|
吸水率 Water absorption rate |
ISO 62 | ||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
-- -- 3 |
MPa | ASTM D638 | |
|
-- -- |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield 4 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
断裂 fracture 4 |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield 4 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
断裂 fracture 4 |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus |
|||
|
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
|
-- -- 6 |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
-- -- 6 , 7 |
MPa | ISO 178 | |
|
屈服，50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 8 |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 8 |
ISO 179/1eU | ||
|
-30℃ -30℃ |
ISO 179/1eU | ||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
-30℃ -30℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
-30℃ -30℃ 9 |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ 9 |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D4812 , ISO 180/1U | ||
|
-30℃ -30℃ |
ASTM D4812 , ISO 180/1U | ||
|
23℃ 23℃ |
ASTM D4812 , ISO 180/1U | ||
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Total Energy 23℃，Total Energy |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火，3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，100 mm跨距 0.45 MPa, unannealed, 100 mm span 10 |
℃ | ISO 75-2/Be | |
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，100 mm跨距 1.8 MPa, unannealed, 100 mm span 10 |
℃ | ISO 75-2/Ae | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ASTM D1525 11 | |
|
B50 B50 |
℃ | ISO 306 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
球压测试 Ball pressure test |
|||
|
125℃ 125℃ |
IEC 60695-10-2 | ||
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ASTM E831 | |
|
MD：23~80℃ MD：23~80℃ |
1/℃ | ISO 11359-2 | |
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ASTM E831 | |
|
TD：23~80℃ TD：23~80℃ |
1/℃ | ISO 11359-2 | |
|
相对温度指数 Relative temperature index |
℃ | UL 746 | |
|
电气性能 Electrical performance |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
介电常数 Dielectric constant |
|||
|
1.10 GHz 1.10 GHz |
ASTM ES7-83 | ||
|
耗散因数 Dissipation factor |
|||
|
1.1 GHz 1.1 GHz |
ASTM ES7-83 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
0.40 mm 0.40 mm |
UL 94 | ||
|
1.70 mm 1.70 mm |
UL 94 | ||
|
2.00 mm 2.00 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
|||
|
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
|
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
透光率 Transmittance |
内部方法 | ||
|
1000 µm 1000 µm |
% | 内部方法 | |
|
2000 µm 2000 µm |
% | 内部方法 | |
|
3000 µm 3000 µm |
% | 内部方法 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.0 in/min |
| 3 类型 1, 2.0 in/min |
| 4 0.051 in/min |
| 5 0.079 in/min |
| 6 Yield |
| 7 80*10*3 sp=62mm |
| 8 80*10*3 |
| 9 120*10*4 mm |
| 10 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
巴斯夫在上海开设新的Catamold卓越中心实验室
2021-07-03 搜料网资讯： 6月30日，巴斯夫宣布在中国上海为其 Catamold 业务开设了一个新的卓越中心实验室。新工厂将成为中国和亚洲其他地区金属注射成型 (MIM) 市场解决方案和产品的专业中心。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付