牌号简介 About |
---|
UNIVAL™ DMDA-6320 NT 7高密度聚乙烯(HDPE)树脂是一种多用途聚合物,设计用于高速生产吹塑容器,用于包装家用工业化学品(如洗涤剂、漂白剂、织物柔软剂)、洗漱用品和化妆品(如洗发水、面霜、乳液等)、保健和医疗辅助用品以及食品。此外,它可以吹塑成其他薄壁零件和家庭用品,并可以挤压成型材。优异的抗应力、抗裂性和刚度、高冲击强度、低膨胀性、良好的熔融强度,含有抗静电剂,符合:加拿大HPFB无异议(有限制)欧盟,2011年10月,美国FDA 21 CFR 177.1520(c)3.2A,美国FDA-DMF,请参考相关法规了解全部细节。 UNIVAL™ DMDA-6320 NT 7 High Density Polyethylene (HDPE) Resin is a multipurpose polymer designed for the high speed production of blow molded containers used to package household industrial chemicals (e.g., detergents, bleach, fabric softeners), toiletries and cosmetics (e.g., shampoos, creams, lotions, etc.), health and medicinal aids, and food products. In addition, it can be blow molded into other thin walled parts and houseware items and can be extruded into profiles. Excellent stress-crack resistance and rigidity High impact strength Low swell Good melt strength Contains antistat Complies with: Canadian HPFB No Objection (with limitations) EU, No 10/2011 U.S. FDA 21 CFR 177.1520 (c) 3.2a U.S. FDA -DMF Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.953 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.46 | g/10min | |
190℃,21.6kg 190℃,21.6kg |
39 | g/10min | |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
50 ℃,100%非离子表面活性剂,F50 50 ℃, 100% non-ionic surfactant, F50 |
40.0 | hr | ASTM D1693 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸冲击强度 Tensile impact strength 2 |
168 | kJ/m² | ASTM D1822 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服 yield |
% | ||
断裂 fracture |
% | ||
弯曲模量 Bending modulus |
|||
正割 Secant |
MPa | ASTM D790-B |
备注 |
---|
1 With limitations |
2 一般属性:这些不能被视为规格。 |
3 类型 S |
【新闻资讯】查看全部
能源化工界急盼利好政策落实
2022-03-05 国家发改委价格司司长万劲松在2月24日的新闻发布会上表示,为进一步完善煤炭市场价格形成机制,促进煤炭价格合理形成,近日国家发改委印发《关于进一步完善煤炭市场价格形成机 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |