牌号简介 About |
---|
Torlon 7130是30%碳纤增强级聚酰胺酰亚胺(PAI)树脂。具有高强度、高模量、卓越的耐蠕变性,以及良好的抗疲劳性。热膨胀特性近似于钢,因此具有优良的尺寸稳定性。 在所有能耐受275 ℃( 525°F )高温的热塑性树脂中,Torlon PAI具有最高的强度和刚度 。并具有优异的耐磨损性、抗蠕变性和耐化学性。 这种树脂可用于金属替代材料、滑动叶片、航空部件、叶轮、导流罩、活塞、外壳等部件。 具有注塑和挤出(E)级。 Torlon® 7130 is an 30% carbon-fiber reinforced grade of polyamide-imide (PAI) resin. It offers high strength and modulus, exceptional creep resistance, and good fatigue resistance. It has thermal expansion characteristics similar to steel, and therefore excellent dimensional stability. Torlon® PAI has the highest strength and stiffness of any thermoplastic up to 275°C (525°F). It has outstanding resistance to wear, creep, and chemicals. The potential applications for this resin include metal replacement, sliding vanes, aerospace parts, impellors, shrouds, pistons, and housings. It is available in injection molding and extrusion (E) grades. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.48 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.0 到 0.15 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.26 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- |
16500 | MPa | ASTM D638 |
-- -- |
22300 | MPa | ASTM D1708 |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D1708 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
断裂 fracture 3 |
% | ASTM D1708 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
23℃ 23℃ |
MPa | ASTM D790 | |
232℃ 232℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
23℃ 23℃ |
MPa | ASTM D790 | |
232℃ 232℃ |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
cm/cm/℃ | ASTM D696 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 以前,ASTM标准试验方法D1708用于测量PAI和类似材料的拉伸性能,因为小试样能节约材料。现在使用最广泛的是ASTM D638 1 Bar 试样 。所含D1708数值仅用作历史参考,不与D638值作对照用。 |
【新闻资讯】查看全部
这家中国500强石化企业,连云港年产135万吨PE等项目一次开车成功!
2021-05-29 搜料网资讯: 5月20日晚间,卫星石化发布公告称,全资子公司连云港石化有限公司年产135万吨PE、219万吨EOE和26万吨ACN联合装置项目一阶段工程,也就是连云港石化一阶段项目,各装置经 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |