| 牌号简介 About |
|---|
| “Moplen”RP225M是一种控制流变介质的改性丙烯无规共聚物，用于生产高透明的铸造薄膜。该产品含有防滑和防堵剂。它具有良好的加工性、透明度和光泽度，并表现出良好的热焊接性。主要应用于食品包装、文具包装、衬衫包装和丝袜包装。它还适用于生产固定式文件夹。”MOPLEN“RP225M适用于食品接触。有关监管信息，请参阅“MOPLEN”RP225M产品管理公告（PSB）。 "Moplen" RP225M is a controlled rheology medium modified propylene random copolymer for manufacturing high transparent cast films. The product contains slip and anti-block agents. It offers good processability, excellent clarity and gloss and exhibits very good heat weldability. Main applications are packaging of foodstuffs, packaging of stationary, shirts and hosiery. It is also suitable for production of stationary folders. "Moplen" RP225M is suitable for food contact. For regulatory information please refer to "Moplen" RP225M Product Stewardship Bulletin ( PSB ). |
产品描述 Product Description
用途：包装;流延薄膜;食品包装;文具;
颜色：清晰/透明
加工条件：流延薄膜
性能特点： 抗结块性; 焊接; 可控流变; 高光滑性; 透光性好; 无规共聚物; 食品接触; 表面光泽度好; 易加工; Excellent Processability,Good Clarity,Good surface appearance,Smoothness,Controllable rheological,High anti-blocking,Food contact compliance,Random copolymer,Welding
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.900 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
8.0 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
700 | MPa | ISO 527-1-2 |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
23.0 | MPa | ISO 527-2/50 |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
12 | % | ISO 527-2/50 |
|
摩擦系数 friction coefficient |
ASTM D1894 | ||
|
与自身 - 动态，铸造薄膜 With oneself - dynamic, casting thin films |
ASTM D1894 | ||
|
与自身 - 静态，铸造薄膜 Compared to itself - static, cast thin films |
ASTM D1894 | ||
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
µm | ||
|
割线模量 Secant modulus 2 |
|||
|
MD，50 µm，铸造薄膜 MD, 50 µ m, cast thin film 2 |
MPa | ASTM D882 | |
|
拉伸强度 tensile strength 3 |
ASTM D882 | ||
|
MD，屈服，50 µm，挤塑薄膜 MD, yield, 50 µ m, extruded film |
MPa | ASTM D882 | |
|
MD，断裂，50 µm，挤塑薄膜 MD, fracture, 50 µ m, extruded film |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain 3 |
ASTM D882 | ||
|
MD，屈服，50 µm，挤塑薄膜 MD, yield, 50 µ m, extruded film |
% | ASTM D882 | |
|
MD，断裂，50 µm，挤塑薄膜 MD, fracture, 50 µ m, extruded film |
% | ASTM D882 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
0℃ 0℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，50.0 µm，铸造薄膜 45 °, 50.0 µ m, cast thin film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
50 µm，铸造薄膜 50 µ m, cast thin film |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 1,2 in/min |
| 3 20 in/min |
|
【新闻资讯】查看全部
Talga Resources与英国 Biomer Technology签署结合开发协议
2018-09-21 总部位于澳大利亚的先进材料技术公司Talga Resources表示，已与英国聚合物制造和技术公司Biomer Technology签署了一项联合开发协议，共同开发石墨烯增强型热塑性塑料，以实现医疗保健领域及涂料市场的潜在商业化。 这项计划是在Talga石墨烯商业化战略下的复合材料领域进行的。JDA的亮点包括：在Biomer聚合物中加入 了Talga功能化石墨烯(“Talphene”)的新型多功能热塑性聚氨酯。 评估条款:在产品商业化和知识产权所有权的情况下 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付