| 牌号简介 About |
|---|
| ML1710SC是一种茂金属线性低密度聚乙烯共聚物。这种茂金属级是为高性能薄膜应用而设计的，要求具有优异的光学性能和韧性。ML1710SC采用工艺助剂和工艺稳定包配制。不含防滑或防堵塞添加剂。薄膜挤出：ML1710SC适用于需要高性能聚乙烯树脂的薄膜应用。用ML1710SC制备的薄膜，透明度高，光泽度高，韧性和密封性好。ML1710SC特别适用于含粘胶添加剂的吹塑拉伸薄膜。这一等级允许快速的黏附发展和更高的最终黏附水平，具有优异的抗穿刺性和韧性。如果预期的应用涉及间歇性到长时间暴露在阳光下，则应考虑添加紫外线稳定剂。 ML1710SC is a metallocene linear low density polyethylene copolymer. This metallocene grade is designed for high performance film applications requiring superior optical properties and toughness. ML1710SC is formulated with a process aid and a process stabilisation package. It does not contain slip or antiblocking additives. Film Extrusion: ML1710SC is intended for film applications requiring high performance polyethylene resins. Films produced with ML1710SC have superior clarity and higher gloss, combined with excellent toughness and sealability. ML1710SC is particularly suitable for blown stretch films containing cling additives. This grade allows rapid cling development and a higher ultimate cling level, with excellent puncture resistance and toughness. Addition of a UV stabiliser should be considered where the intended application involves intermittent to extended exposure to sunlight. |
产品描述 Product Description
用途：薄膜;吹膜;
加工条件：薄膜挤出 Film extrusion
性能特点： 共聚物; 透光性好; 光学性能; 耐候抗UV; 表面光泽度好; 韧性好; 低密度; 抗穿孔性; 易加工; Weather resistance is good,Excellent Processability,Good Clarity,Good flexibility,Good surface appearance,Low density,Copolymer,Puncture Resistant
紫外线：UV Stabilized
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.917 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
1.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
50 | µm | |
|
割线模量 Secant modulus 2 |
|||
|
2% 正割，MD：50 µm 2% secant, MD: 50 µ m |
140 | MPa | |
|
2% 正割，TD：50 µm 2% secant, TD: 50 µ m |
140 | MPa | |
|
拉伸强度 tensile strength 3 |
|||
|
MD，屈服，50 µm MD, yield, 50 µ m |
MPa | ||
|
TD，屈服，50 µm TD, yield, 50 µ m |
MPa | ||
|
MD，断裂，50 µm MD, fracture, 50 µ m |
MPa | ||
|
TD，断裂，50 µm TD, fracture, 50 µ m |
MPa | ||
|
拉伸应变 Tensile strain 3 |
|||
|
MD，断裂，50 µm MD, fracture, 50 µ m |
% | ||
|
TD，断裂，50 µm TD, fracture, 50 µ m |
% | ||
|
落锤冲击 Drop hammer impact 4 |
|||
|
50 µm 50 µm 4 |
g | ASTM D1709 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
|
MD：50 µm MD：50 µm |
g | ||
|
TD：50 µm TD：50 µm |
g | ||
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，50 µm 45°，50 µm |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
50 µm 50 µm |
% | ASTM D1003 | |
| 备注 |
|---|
| 2、20 mm/min |
| 3、500 mm/min |
| 4、F50 |
|
【新闻资讯】查看全部 
英国公司强强联手，促使石墨烯加强复合资料新时代到来…
2017-08-28 位于英国安曼福德的高级材料公司Haydale和英国南安普敦的罗杰斯先进复合材料公司(该公司简称RAC)目前在复合材料领域进行技术上和商业上的合作，旨在开发出先进的石墨烯增强复合材料。 其中，RAC目前正在开发一个复合材料中心(该中心地处于靠近英国南海岸的索伦特)。而且，也正是由于二者的在技术上和商业上的合作，将使得RAC公司能够访问Haydale公司在复合材料，聚合物和树脂方面的广泛技术知识，并将Haydale开发的先进石墨烯增强复合材料系列纳入其公司目前及未来的研究项目。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |