牌号简介 About |
---|
它是热塑性弹性体(TPE)系列中的一种软质、黑色、抗紫外辐射的热塑性硫化弹 性体(TPV)。这种材料适用于要求低雾化和良好外观的汽车内饰应用。这一牌号 的山都平 TPV 是剪切速率依赖型产品,可在常规热塑性注塑成型设备上加工。这 是一种聚烯烃基材料,可在生产过程中进行回收利用。 A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material is designed for automotive interior applications requiring low fogging and good appearance. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding. It is polyolefin based and recyclable within the manufacturing stream. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D792 |
密度 Density |
0.920 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
6.60 | MPa | ISO 37 |
TD,断裂,23℃ TD, fracture, 23 ℃ |
6.60 | MPa | ASTM D412 |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
2.30 | MPa | ISO 37 |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ISO 37 | |
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ASTM D412 | |
压缩形变 Compression deformation |
ASTM D395B | ||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
100℃,70 hr 100℃,70 hr |
% | ASTM D395B | |
压缩形变 Compression deformation |
ISO 815 | ||
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
100℃,70 hr 100℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,15 秒,23℃ Shore A, 15 seconds, 23 ℃ |
ISO 868 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
脆化温度 Embrittlement temperature |
℃ | ISO 812 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度的变化率 在空气中(100℃,1008 hr) The rate of change in tensile strength in air (100 ℃, 1008 hr) |
% | ASTM D573 | |
拉伸强度的变化率 在空气中(100℃,1008 hr) The rate of change in tensile strength in air (100 ℃, 1008 hr) |
% | ISO 188 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
100℃,1008 hr 100℃,1008 hr |
% | ASTM D573 | |
Change in Tensile Strain at Break in Air(100℃,1008 hr) Change in Tensile Strain at Break in Air(100℃,1008 hr) |
% | ISO 188 | |
Change in Durometer Hardness in Air(邵氏 A,100℃,1008 hr) Change in Durometer Hardness in Air (100 ℃, 1008 hr) |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
|||
邵氏 A,100℃,1008 hr Shore A, 100 ℃, 1008 hr |
ISO 188 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1 |
3 类型 A |
【新闻资讯】查看全部
美国软体家具行动委员会(UFAC)修订了易燃性测试
2021-07-16 搜料网资讯: 美国软垫家具行动委员会 (UFAC) 最近宣布已修订其长期家具可燃性测试和验证计划,以更好地支持其成员公司满足 6 月 25 日生效的要求。新的联邦法律 COVID-19 监管救济和在 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |