牌号简介 About |
---|
NGL070LG是一种基于丁烯共单体的线性低密度聚乙烯树脂,由IEPL使用加拿大杜邦(现为Nova Chemicals)的“SClairtech”溶液聚合工艺生产,用于挤压涂层应用。作为一种共聚物,它在薄挤压涂层中具有优异的环境应力、抗裂性、撕裂强度、耐磨性、韧性、粘合性和密封性。 NGL070LG is a Butene co-monomer based Linear Low Density Polyethylene Resin manufactured by IEPL using "SCLAIRTECH" solution polymerisation process of DU Pont, Canada (Now Nova Chemicals) designed for extrusion coating application. As a copolymer it offers excellent environmental stress crack resistance, tear strength, abrasion resistance, toughness, adhesion and sealing properties in a thin extrusion coating. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.926 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
7.0 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
750 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
106 | ℃ | ASTM D1525 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
60 | ASTM D2240 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
摩擦系数 friction coefficient |
ASTM D1894 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
明年亚洲TDI面临低位盘整
2015-12-28 由于市场需求疲软,业内人士预计明年亚洲甲苯二异氰酸酯(TDI)市场仍将处于供过于求的状况。 因价格低迷,自2014年起,一些东北亚TDI生产商一直亏损。今年的现货价格持续下跌至多年来的最低点。市场人士分析,亚洲TDI价格可能会持稳到明年1月,可能会在农历新年之前,买盘兴趣出现小幅回升。 据悉,今年7~9月,一些生产商曾试图通过关闭装置而收紧供应,并在2015年大部分时间降低开工率,但未能推动市场价格上涨。由于市场状况不佳,日本三井化学决定在明年3月底永久关闭 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |