公司信息及水印
牌号简介 About |
---|
LNP Lubricomp UFL36AS化合物LNP Lubricomp UFL36AS是一种含有30%玻璃纤维、15%聚四氟乙烯的聚邻苯二甲酰胺(PPA)基树脂。这种材料的附加特性是:热稳定,耐磨。也称为:LNP*Lubricomp*化合物UFL-4036 A HS产品重新订购名称:UFL36ASLNP Lubricomp UFL36AS化合物LNP Lubricomp UFL36AS是一种基于含玻璃纤维、聚四氟乙烯的聚邻苯二甲酰胺树脂的化合物。附加功能包括内部润滑、热稳定。又名:lnp*lubricomp*化合物UFL-4036 A HS产品再订购名称:UFL36AS LNP LUBRICOMP UFL36AS is a Polyphthalamide (PPA) base resin containing 30% Glass Fiber, 15% PTFE. Added features of this material are: Heat Stabilized, Wear Resistant. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.58 | g/cm³ | ASTM D792 |
密度 Density |
1.57 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
TD:24 hrs TD:24 hrs |
0.80 to 1.0 | % | ASTM D955 |
MD:24 hrs MD:24 hrs |
0.20 to 0.40 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.25 | % | ISO 62 |
24hr,50% RH 24hr,50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ASTM D638 | ||
-- -- 2 |
MPa | ASTM D638 | |
-- -- 3 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 4 |
|||
断裂 fracture |
MPa | ISO 527-2/5 | |
断裂 fracture 4 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
屈服 yield 4 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 4 |
|||
断裂 fracture |
% | ISO 527-2/5 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
屈服 yield 4 |
% | ASTM D638 | |
弯曲模量 Bending modulus 6 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 |
|||
断裂,50 mm跨度 Fracture, 50 mm span 5 |
MPa | ASTM D790 | |
屈服,50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
摩擦系数 friction coefficient |
ASTM D3702 Modified | ||
动态 dynamic |
ASTM D3702 Modified | ||
静态 static state |
ASTM D3702 Modified | ||
磨损因数 Wear factor |
ASTM D3702 Modified | ||
Ring Ring |
10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified | |
Washer Washer |
10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ 7 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 7 |
|||
23℃ 23℃ 7 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 8 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-30~30℃ TD:-30~30℃ |
1/℃ | ASTM D696 | |
MD:-30~30℃ MD:-30~30℃ |
1/℃ | ASTM D696 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 2.0 in/min |
4 类型 1, 0.20 in/min |
5 0.051 in/min |
6 0.079 in/min |
7 Yield |
8 2 mm/min |
9 80*10*3 |
10 80*10*4 |
11 80*10*4 mm |
【新闻资讯】查看全部
马来西亚制定18项废塑料入口准证新条例
2018-11-19 马来西亚房屋及地方政府部长祖莱达14日表示,政府已经制定18项废塑料入口准证新条例,政府只允许5个国家和地区的废塑料入口,即美国、英国、日本、澳洲和欧洲,其他的一律不淮。 在马来西亚政府冻结废塑料入口准证期间,共有200多个货柜停滞在北海北岸箱运码头,目前仍有175个货柜停滞在此且未向海关申报,祖莱达在码头视察和聆听汇报会后在记者会说,业者必须先向房屋及地方政府部申报废塑料来自哪个国家,而拥有废塑料入口准证的业者,可以依据18项新条例,向该局重新申报,即可索回货柜。对于17 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |