牌号简介 About |
---|
不含卤素和红磷的阻燃玻璃纤维增强注塑等级;颜色浅,具有优异的机电性能。 Without halogenes and red phosphorus a flame retarded glass fiber reinforced injection moulding grade; light in colour with outstanding mechanical and electrical properties. |
技术参数 Technical Data | |||
---|---|---|---|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
|||
注塑/挤出 Injection molding/extrusion |
280 - 300 | ℃ | |
热变形温度 Hot deformation temperature |
|||
1.8 MPa 1.8 MPa |
245 | ℃ | ISO 75-1/2 |
0.45 MPa 0.45 MPa |
260 | ℃ | ISO 75-1/2 |
高温极限,2000h,抗拉强度降低50% High temperature limit, 2000h, reduced tensile strength by 50% |
130 | °C | IEC 60216 |
高温极限,5000h,抗拉强度降低50% High temperature limit, 5000h, reduced tensile strength by 50% |
155 | °C | IEC 60216 |
可燃性(UL-黄牌-见附件) Flammability (UL Yellow Label - see attachment) |
|||
GWFI(厚度) GWFI (thickness) |
°C(mm) | IEC 60695-2-12 | |
GWIT(厚度) GWIT (thickness) |
°C(mm) | IEC 60695-2-12 | |
铁路:危险等级acc,R22和R23 Railway: danger levels acc, R22, and R23 |
等级 | EN 45545-2 | |
相对电容率 Relative permittivity |
|||
1 MHz 1 MHz |
IEC 60250 | ||
耗散系数 Dissipation coefficient |
|||
1MHz 1MHz |
E-4 | IEC 60250 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
CTI,解决方案A CTI, Solution A |
- | IEC 60112 | |
机械性能 MECHANICAL |
|||
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸应变 Tensile strain |
% | ISO 527-1-2 | |
拉伸断裂 |
MPa | ISO 527-1/-2 | |
抗弯强度 Bending strength |
MPa | ISO 527-1/-2 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
MPa | ISO 527-1-2 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
粘度值 Viscosity value |
|||
5%于96%H2SO4 5% to 96% H2SO4 |
cm³/g | ISO 307, 1157, 1628 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
吸湿率 Moisture absorption rate |
|||
平衡,23℃,50%RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
融化温度,DSC Melting temperature, DSC |
°C | ISO 11357-1/-3 | |
熔体体积流动速率 Melt Volume Rate |
|||
275℃,5 kg 275℃,5 kg |
cm³/10min | ISO 1133 | |
模具温度,注塑成型 Mold temperature, injection molding |
°C | - | |
收缩率 Shrinkage rate |
|||
MD MD |
% | ISO 294-4 | |
TD TD |
% | ISO 294-4 | |
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
-30℃ -30℃ |
kJ/m² | ISO 179/1eU |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20000 h |
3 5000 h |
4 Limited validity period |
5 NF X70-100-1/-2 |
【新闻资讯】查看全部
河南省塑料协会正式挂牌成立
2016-02-03 在中国塑协和河南省相关厅局的大力支持下, 河南省塑料协会经河南省民政厅2015年12月24日正式批准成立,并依法取得社会团体法人资格。结束了十几年河南省没有塑料行业团体组织的历史。 河南省塑料协会是由河南省中原塑料机械有限公司、郑州轻工业学院、河南省工业大学、郑州大学郑工橡塑模具国家工程研究中心、河南洋浦科贸有限公司、郑州海天机械销售有限公司、河南鑫涌塑料化工防腐有限公司、新乡市金泉塑胶制品有限公司等100多家创会会员及个人会员发起组织创建。河南省中原塑料机械有限公司董事长 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |