| 碳纤维增强，石墨和聚四氟乙烯填充聚醚酮VESTAKEEP® 2000 FC30是一种中等粘度，碳纤维增强，石墨和聚四氟乙烯填充聚醚酮用于注塑成型。该树脂制成的零件由于具有自润滑作用，可用于轴承衬套或齿轮箱零件。半结晶聚合物具有优异的机械、热和化学抗性。VESTAKEEP® 2000 FC30制造的零件是自动灭火的。VESTAKEEP® 2000 FC30可由热塑性塑料常用的注塑机加工。我们建议在注塑过程中，熔融温度在370°C到380°C之间。如果温度超过380°C，会释放有毒气体。必须提供足够的通风和保护设备。模具温度应在160°C至200°C的范围内，最好是180°C。 Carbon fiber-reinforced, graphite and PTFE-filled polyether ether ketone VESTAKEEP 2000 FC30 is a medium-viscosity, carbon fiber-reinforced, graphite and PTFEfilled polyether ether ketone for injection molding. Parts made of this resin can be used for bearing bushing or gearbox parts, due to the self-lubricating effect. The semi-crystalline polymer features superior mechanical, thermal, and chemical resistance. Parts made from VESTAKEEP 2000 FC30 are self-extinguishing. VESTAKEEP 2000 FC30 can be processed by common injection-molding machines for thermoplastics. We recommend a melt temperature between 370°C and 380°C during the injection molding process. If temperatures exceed 380°C, toxic gases can be released. Adequate ventilation and protective equipment must be provided. The mold temperature should be within a range of 160°C to 200°C, preferably 180°C. |
产品描述 Product Description
用途：轴承;衬套;齿轮;
加工条件：注射成型 Injection Molding
性能特点： 半结晶; 防火阻燃等级V-0; 自润滑; 耐化学性; 自熄; Self-lubricating,Self-extinguishing,Hypocrystalline,Solvent resistance,V-0
填料：PTFE/碳纤维/石墨
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.45 | g/cm³ | ISO 1183 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
380℃，5 kg 380℃，5 kg |
15.0 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate 2 |
ISO 294-4 | ||
|
TD：180℃，2.0 mm TD：180℃，2.0 mm |
0.40 | % | ISO 294-4 |
|
MD：180℃，2.0 mm MD：180℃，2.0 mm |
0.10 | % | ISO 294-4 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
11500 | MPa | ISO 527-2 |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃，完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 179/1eA | |
|
23℃，完全断裂 23 ℃, completely fractured |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-30℃，完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
|
23℃，完全断裂 23 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ISO 306/A | |
|
-- -- |
℃ | ISO 306/B | |
|
熔融温度 Melting temperature 5 |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：23~55℃ MD：23~55℃ |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
相对电容率 Relative permittivity |
IEC 60250 | ||
|
50 Hz 50 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
1.60 mm 1.60 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
|||
|
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
|
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 determined on 2 mm sheets with film gate at rim mold temperature 180°C |
| 3 2nd heating |
|
【新闻资讯】查看全部 
环氧树脂业务下滑！2022年第二季度，Olin的净收入为4.221亿美元
2022-08-01 7月28日，Olin公布了截至2022年6月30日的第二季度财务业绩：2022年第二季度销售额为2.611亿美元，比去年同期的22.213亿美元增长了17.8%；2022年第二季度报告的净收入为4.221亿美元，比去年同 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付